高强机制砂混凝土抗压性能试验研究

发布时间：2018-01-07 05:14

本文关键词：高强机制砂混凝土抗压性能试验研究　出处：《华北水利水电大学学报(自然科学版)》2014年05期 　论文类型：期刊论文

【摘要】：选用工程常用的机制砂、粉煤灰、高效减水剂配制绿色高强混凝土,通过试验研究了砂率、粉煤灰掺量、骨料最大粒径等因素对机制砂混凝土拌合物的工作性能和抗压性能的影响.混凝土配合比采用水胶比为0.31,0.28;砂率为29%,31%,33%,35%;粉煤灰掺量为0%,25%,35%,45%;碎石最大粒径为5,10,16,20 mm.结果表明:采用砂率33%、粉煤灰掺量最佳范围为25%~35%、碎石粒径为5~20 mm的连续级配碎石,可配制满足结构工程用C50~C80高强机制砂混凝土.研究成果为同类工程建设提供了科学依据.
[Abstract]:The mechanism of sand, engineering commonly used fly ash and superplasticizer preparation of green high strength concrete, sand ratio are studied by means of experiment, the amount of fly ash, effect of maximum aggregate size and other factors on the mechanism of sand concrete mixture workability and compressive properties of concrete mix. The water binder ratio of the sand ratio is 0.31,0.28; 29%, 31%, 33%, 35%; the amount of fly ash was 0%, 25%, 35%, 45%; aggregate maximum particle size of 5,10,16,20 mm. results show that the sand ratio 33%, the amount of fly ash the optimum range of 25%~35%, particle size of gravel graded crushed stone 5~20 mm, can be made of C50~C80 high strength concrete with machine-made sand meet the engineering structure. The research results provide a scientific basis for similar engineering construction.

【作者单位】：焦作市公路管理局;华北水利水电大学土木与交通学院;
【基金】：新型城镇建筑技术河南省协同创新中心(教科技[2013]638号) 生态建筑材料与结构工程河南省高校科技创新团队(13IRTSTHN002)科研课题
【分类号】：TU528
【正文快照】： 随着对自然环境和天然河道保护的重视,机制砂已逐渐成为替代天然砂的主要人工资源.目前对采用机制砂配制常用强度等级混凝土的研究已较为成熟,并得到了广泛的工程应用[1-3].如王稷良[4]研究了机制砂中石粉含量及机制砂的粒形、级配、压碎值等机制砂特性指数对混凝土性能的影响

【参考文献】