不同骨料掺量与级配下白钨尾矿-偏高岭土基地聚合物的制备及其早期强度

发布时间：2018-01-16 00:15

本文关键词：不同骨料掺量与级配下白钨尾矿-偏高岭土基地聚合物的制备及其早期强度　出处：《硅酸盐通报》2015年12期 　论文类型：期刊论文

【摘要】：将富含Si、Ca的白钨尾矿和富含Si、Al的偏高岭土复合作为硅铝原料(基质),在水玻璃激发作用下制备地聚合物砂浆,以调整骨料掺量与级配的方式去优化试样的早期抗压强度;并借助XRD和SEM-EDS对优选试样的微结构进行表征。结果表明:当骨料掺量为50%时,产生高强度砂浆试样的个数最多;当骨料掺量为40%,且细、中、粗骨料在总骨料中分别占10%、60%、30%时,试样的早期抗压强度获得最高值26.7 MPa;在对硅铝原料进行的活化预处理和水玻璃激发以及对砂浆试样进行的蒸压养护之后,硅铝原料中的Si、Al、Ca等元素得以部分溶出,参与形成地聚合物凝胶体,赋予砂浆试样良好的早期强度性能。
[Abstract]:Si-Ca rich scheelite tailings and Si-Al rich metakaolin were used as silica-aluminum raw materials (matrix) to prepare polymer mortar under the action of water glass excitation. The early compressive strength of the sample was optimized by adjusting the aggregate content and gradation. The microstructure of the selected samples was characterized by XRD and SEM-EDS. The results showed that when the amount of aggregate was 50%, the number of high strength mortar samples was the most. When the amount of aggregate is 40 and fine, coarse aggregate accounts for 10% of the total aggregate and 30% of the total aggregate, the maximum value of early compressive strength of the sample is 26.7 MPA; After activation pretreatment, water glass excitation and autoclaved curing of the mortar sample, the Si-Al ~ (2 +) Ca and other elements in the Si-Al raw material can be partially dissolved. Participating in the formation of geopolymer gels to give mortar samples good early strength properties.
【作者单位】：江西理工大学江西省矿业工程重点实验室;江西理工大学工程研究院;江西理工大学资源与环境工程学院;
【基金】：国家科技支撑计划项目(2012BAC11B07) 江西省教育厅科技项目(GJJ14426) 江西省自然科学基金资助项目(20142BAB216008) 江西省科技支撑计划项目(20151BBG70015) 江西理工大学科研基金重点课题(NSFJ2014-K01) 国家自然科学基金项目(51264009)
【分类号】：TU528
【正文快照】： 1引言地聚合物(Geopolymer)是一种通过硅铝质材料与激发剂在常温或一定养护条件下经“溶解-单体重构-缩聚”反应凝结硬化而成的具有类沸石结构的新型胶凝材料,其中“激发剂”可以是碱硅酸盐溶液[1-3]、MOH(M=Na或K)溶液[4-6]或磷酸溶液[7-10]等。它在制备过程中的节能环保特性