中盐安徽红四方新型建材科技有限公司蒸压α型高强石膏砌块生产线投产

发布时间：2018-04-14 23:38

  本文选题：高强石膏 + 蒸压　； 参考：《新型建筑材料》2015年10期

【摘要】：正日前,由中盐安徽红四方新型建材科技有限公司投资建设的全国最大蒸压α型高强石膏砌块生产线在合肥建成投产,该项目坐落于合肥市肥东县合肥循环经济示范园,总投资1.45亿元。一期可年产56万m~3蒸压α型高强石膏砌块,每年可综合利用磷石膏140万t、电石渣26万t,粉煤灰22万t。二期项目预计2016年底建成。该项目的建成投产,除了将红四方公司每年排放的固体废弃物消化掉,每年还可以消耗陈年堆放的磷石膏近百万
[Abstract]:A few days ago, the largest autoclaved 伪 type high strength gypsum block production line invested by Zhongyan Anhui Hongsi New Building Materials Technology Co., Ltd. was built and put into production in Hefei. The project is located in Hefei Circular economy demonstration Park in Feidong County, Hefei City.The total investment is 145 million yuan.The first stage can produce 560000 mm3 autoclaved 伪 -type high strength gypsum block, and can make comprehensive use of phosphogypsum 1.4 million t, carbide slag 260000 t, fly ash 220000 t per year.The second phase project is expected to be completed by the end of 2016.The completion and commissioning of the project will not only digest the solid waste discharged annually by Red Sifang, but also consume nearly 1 million phosphogypsum stacks each year.
【分类号】：TU522.3;TQ177.3

【相似文献】

相关期刊论文 前10条

1 尹文萱;开辟石膏综合利用新途径[J];煤炭工程;2004年06期

2 屈志中;;高强石膏的缓凝剂[J];建材工业信息;1985年18期

3 刺祚业;;高强石膏在我省试产成功[J];山西建筑;1991年04期

4 王志,邹爱红,李国忠,岳文海;高强石膏材料研究最新进展[J];新型建筑材料;1999年09期

5 秦鸿根;刘小琴;段珍华;唐修仁;;矿物改性剂对高强石膏制品耐水性能的影响[J];建筑砌块与砌块建筑;2010年03期

6 姚启均;;高强石膏[J];建材工业信息;1990年19期

7 张雷,邹妍;免烧高强石膏砖的研制[J];砖瓦;1994年01期

8 金左培;掺加S型减水石膏缓凝剂及促硬剂制备高强石膏[J];上海建材;1995年03期

9 尹文轩,陈周灵;添加外加剂降低α高强石膏膨胀率的研究[J];江苏建材;1996年01期

10 ;高强石膏瓷片的制作[J];中小企业科技信息;1999年10期

相关会议论文 前3条

1 韩灵翠;王永昌;;高强石膏的生产工艺及其能耗比较[A];2014中国建筑材料联合会石膏建材分会第五届年会暨第九届全国石膏技术交流大会及展览会论文集[C];2014年

2 邹其;邓最亮;傅乐蜂;;不同减水剂对高强石膏粉的分散性能及应用性能影响[A];2013中国建筑材料联合会石膏建材分会第四届年会暨第八届全国石膏技术交流大会及展览会论文集[C];2013年

3 韩灵翠;王永昌;;立式蒸压釜采用水热法工艺生产高强石膏[A];2013中国建筑材料联合会石膏建材分会第四届年会暨第八届全国石膏技术交流大会及展览会论文集[C];2013年

相关硕士学位论文 前2条

1 孟雪桦;高强石膏的凝结膨胀性能研究[D];青岛理工大学;2012年

2 王洪霞;化学法制备加气石膏材料的研究[D];北京交通大学;2014年

，

本文编号：1751560