渗透型流体修补砂浆的配制及性能研究

发布时间：2018-06-01 13:32

  本文选题：纳米渗透 + HCC　； 参考：《新型建筑材料》2015年12期

【摘要】：研究了胶凝材料、高活性物质、化学添加剂用量对HCC渗透型修补砂浆本体强度、粘结性能及其耐候性的影响,通过SEM分析了修补砂浆水化物在不同龄期的晶体生长过程,得出了HCC渗透型修补砂浆的最优配比。试验结果表明,按最优配比制备的HCC渗透型修补砂浆具有很好的技术性能和施工性能,符合或优于JG/T 336—2011《混凝土结构修复用聚合物水泥砂浆》标准中A型的要求。
[Abstract]:The effects of cementitious materials, high active substances and chemical additives on the bulk strength, adhesive properties and weathering resistance of HCC permeable repair mortar were studied. The crystal growth process of repaired mortar hydrates at different ages was analyzed by SEM. The optimum ratio of HCC permeable repair mortar is obtained. The experimental results show that the HCC permeable repair mortar prepared with the optimal ratio has good technical and construction properties, which meets or is superior to the requirement of type A in the standard of JG/T 336-2011 "Polymer cement mortar for the repair of concrete structures".
【作者单位】： 南京沪联新型建材有限公司;
【分类号】：TU578.1

【相似文献】

相关期刊论文 前3条

1 王元曦;;水基渗透型无机防水剂的应用现状与前景[J];安徽建筑;2013年04期

2 朱国锋;;路桥水性渗透型无机防水剂防水工程施工要点[J];黑龙江水利科技;2012年08期

3 ;[J];;年期

相关会议论文 前1条

1 沈春林;褚建军;;国家行业标准建材《水性渗透型无机防水剂》(JCT1018—2006)解读[A];全国第九次防水材料技术交流大会论文集[C];2007年

相关重要报纸文章 前1条

1 胡品;超渗透型防水剂[N];中国房地产报;2004年

，

本文编号：1964353