碳硫硅钙石和钙矾石的稳定性

发布时间：2018-02-05 04:05

  本文关键词： 硫酸盐侵蚀 碳硫硅钙石 钙矾石 合成 稳定性　出处：《硅酸盐学报》2016年02期 　论文类型：期刊论文

【摘要】：采用化学方法合成出纯的碳硫硅钙石和钙矾石,对比研究了二者的稳定性。结果显示:钙矾石比碳硫硅钙石更易受到碳酸钠破坏;碳硫硅钙石与氯化钡几乎不发生反应,钙矾石则较易被氯化钡破坏;在碳化条件下,钙矾石较易分解,碳硫硅钙石则几乎没变化。碳硫硅钙石在碳酸钠或氯化钡溶液中的稳定性、热分解稳定性和碳化稳定性均明显高于钙矾石,可能是由于碳硫硅钙石结构中离子键和氢键强度高于钙矾石。
[Abstract]:The stability of pure carbonite and ettringite was studied by chemical method. The results show that ettringite is more vulnerable to the destruction of sodium carbonate than sodalite. There is almost no reaction between calcium carbonate and barium chloride, while ettringite is easily destroyed by barium chloride. Under the condition of carbonization, ettringite is easy to decompose, while carbonite has little change. The stability, thermolysis stability and carbonization stability of carbonite in sodium carbonate or barium chloride solution are obviously higher than that of ettringite. It is possible that the strength of ionic bond and hydrogen bond is higher than that of ettringite.
【作者单位】： 烟台大学环境与材料工程学院;
【基金】：国家自然科学基金(No.51272222)资助项目
【分类号】：TU528
【正文快照】： 尽管对混凝土硫酸盐侵蚀的研究已逾百年,但对相关机理和防治措施尚未完全阐述清楚。正如Neville所描述的那样:“混凝土硫酸盐侵蚀依然是一个混乱的世界”[1]。硫酸盐侵蚀主要包括石膏型、钙矾石型和碳硫硅钙石型侵蚀。相比石膏型和钙矾石型侵蚀,人们对碳硫硅钙石型侵蚀认识相

【相似文献】

相关期刊论文 前6条

1 高礼雄;杜雪刚;孔丽娟;;碳硫硅钙石形成机制的定量分析[J];硅酸盐学报;2012年05期

2 高礼雄,姚燕,王玲;温度对碳硫硅钙石形成的影响[J];硅酸盐学报;2005年04期

3 马保国;付浩兵;王迎斌;田振;;Mg~(2+)离子含量对低温下生成碳硫硅酸钙的影响[J];武汉理工大学学报;2014年06期

4 胡明玉,唐明述;碳硫硅钙石对混凝土的破坏作用[J];混凝土;2001年06期

5 杨长辉;张靖;叶建雄;陈科;吴芳;黄洪胜;杨魁;;水泥基材料碳硫硅钙石型硫酸盐腐蚀[J];混凝土;2009年10期

6 ;[J];;年期

相关硕士学位论文 前2条

1 孟庆业;水泥基胶凝材料中碳硫硅钙石的形成研究[D];中南大学;2014年

2 丁天;碳硫硅钙石结构鉴定及特性研究[D];烟台大学;2014年

，

本文编号：1492070