芳纶表面改性及其与丁腈橡胶复合材料的性能研究

发布时间：2018-01-01 06:03

本文关键词：芳纶表面改性及其与丁腈橡胶复合材料的性能研究　出处：《材料导报》2016年20期 　论文类型：期刊论文

【摘要】：为增强对位芳纶纤维(PPTA)与丁腈橡胶(NBR)之间的界面粘结强度,采用多巴胺(DA)-硅烷偶联剂对芳纶纤维联合改性并制备PPTA/NBR复合材料。结果表明,纤维改性后表面粗糙度增加;表面元素含量和种类都发生较大变化;在H试样抽出测试中,改性后的PPTA帘线/NBR试样抽出力相对于未改性试样增大64.02%,且黏附橡胶较多。改性后的PPTA/NBR试样,纤维含量相同时,断裂伸长率和拉伸强度相对未改性的PPTA/NBR试样增大;随着纤维含量的增加,使用同种方法处理的PPTA/NBR复合材料断裂伸长率减小,拉伸强度先增大后减小。
[Abstract]:In order to strengthen the interfacial bond strength between PPTAA and NBR). The aramid fiber was modified by dopamine dada-silane coupling agent and the PPTA/NBR composite was prepared. The results showed that the surface roughness of the fiber increased after modification. The content and species of surface elements changed greatly. In the H specimen extraction test, the extracted force of the modified PPTA cord / NBR specimen increased 64.02% compared with the unmodified sample, and the adhesive rubber was more than that of the modified PPTA/NBR sample. When the fiber content is the same, the elongation at break and tensile strength of unmodified PPTA/NBR specimen increase. With the increase of fiber content, the elongation at break and tensile strength of PPTA/NBR composites treated by the same method decreased firstly and then decreased.
【作者单位】：宁波大学材料科学与化学工程学院;宁波大学宁波市特种高分子材料制备与应用技术重点实验室;
【基金】：国家自然科学基金(21274070) 宁波市“3315计划”高端创业创新团队(A类)(2012S0001) 宁波市科技局/农业与社会发展攻关项目(2011A31002) 浙江省重点科技创新团队计划(2011R50001) 宁波市特种高分子材料制备与应用技术重点实验室(2014A22001) 浙江省科技创新团队子项(019-E01176124200) 宁波大学研究生科研创新基金
【分类号】：TQ342.72;TB332
【正文快照】： 用技术重点实验室,宁波315211)闫智敬:女,1991年生,硕士生,主要研究方向为芳纶表面改性及其复合材料性能E-mail:276511397@qq.com陈忠仁:通讯作者,男,博士,教授,博士生导师,主要研究方向为高分子复合材料等E-mail:chenzhongren@nbu.edu.cn0引言短纤维增强橡胶复合材料(Short f