铁酸镍在膨胀阻燃聚乳酸复合材料中的作用

发布时间：2018-01-07 04:10

本文关键词：铁酸镍在膨胀阻燃聚乳酸复合材料中的作用　出处：《塑料》2017年04期 　论文类型：期刊论文

【摘要】：利用水热法制备了铁酸镍(NiFe_2O_4)纳米粒子,基于生物可降解材料聚乳酸(PLA)的易燃性,将NiFe_2O_4纳米粒子作为协效剂与膨胀型阻燃剂(IFR)复配,应用于PLA的阻燃改性。结果表明,所有的PLA复合材料均达到UL-94 V-0级别,LOI显著提高至39%以上;NiFe_2O_4纳米粒子有助于PLA膨胀阻燃体系形成更为膨胀和相对致密的炭层,明显提高炭渣中有序化炭的含量,有效提高PLA膨胀阻燃体系的初始降解温度,并显著提高其成炭量。因此,NiFe_2O_4纳米粒子在PLA膨胀阻燃体系中具有良好的协效作用,能够显著提高PLA膨胀阻燃体系的热稳定性和阻燃性能。
[Abstract]:Nickel ferrite were prepared by hydrothermal synthesis method (NiFe_2O_4) nanoparticles, biodegradable polylactic acid (PLA) based on the flammability of NiFe_2O_4 nanoparticles as synergistic agent and intumescent flame retardant (IFR) was used in flame retardant modification of PLA. The results show that the PLA composite material all reached UL-94 V-0 level LOI, increased to more than 39%; NiFe_2O_4 nanoparticles contribute to the formation of PLA is more expansive and relatively dense carbon layer of intumescent flame retardant system, significantly increased the content of the ordered carbon carbon residue, effectively improve the PLA expansion of the initial degradation temperature of flame retardant system, and significantly improve the carbonresidue. Therefore, NiFe_2O_4 nanoparticles in PLA the expansion has obvious synergistic effect of flame retardant system, can significantly improve the thermal stability and flame retardant properties of PLA intumescent flame retardant system.

【作者单位】：常州大学环境与安全工程学院;常州大学材料科学与工程学院;
【基金】：江苏省高校自然科学研究项目(15KJB620001)
【分类号】：TB332
【正文快照】： 可生物降解材料聚乳酸(PLA)具有优良的力学性能和加工性能,有望代替石油基不可生物降解的高分子材料应用于汽车、航空、电子产品等领域,具有良好的市场应用前景[1-2]。然而,由于PLA是聚酯类化合物,其氧指数(LOI)仅为20%,且垂直燃烧测试(UL-94)结果较差[3],具有较大的火灾隐患,

【相似文献】