泡沫金属夹层厚度对压印连接强度的影响

发布时间：2018-01-08 08:27

  本文关键词：泡沫金属夹层厚度对压印连接强度的影响　出处：《特种铸造及有色合金》2017年08期 　论文类型：期刊论文

  更多相关文章： 压印连接 泡沫金属 拉伸-剪切试验 断口分析

【摘要】：分别对添加1.0、1.5、2.0mm泡沫铜夹层的5052Al-泡沫铜-5052Al"三明治"板进行压印连接,对连接好试件的截面进行直观检测,分析接头成形质量;通过拉伸-剪切试验,分析接头的载荷承载能力和能量吸收能力;对失效后的接头断口进行扫描,从微观层面分析接头失效机理。结果表明,泡沫铜夹层厚度增加导致颈部厚度增加,镶嵌量减少,载荷承载能力相应提高,但对能量吸收能力影响不大,接头失效形式为颈部断裂,微观断裂特征为韧窝断裂。
[Abstract]:The 5052Al- foam copper-foam "sandwich" plate with 1.0 ~ 1.5mm foam copper sandwich was imprinted respectively, and the section of the specimen was directly inspected. Analysis of joint forming quality; The load-carrying capacity and energy absorption capacity of the joint are analyzed by tensile and shear tests. The fracture surface of the joint after failure is scanned and the failure mechanism of the joint is analyzed from the microcosmic level. The results show that the thickness of the foam copper interlayer increases the thickness of the neck increases the amount of inlay decreases and the load-bearing capacity increases accordingly. However, it has little effect on the energy absorption ability. The failure mode of the joint is neck fracture, and the microfracture characteristic is dimple fracture.
【作者单位】： 昆明理工大学机电工程学院;
【基金】：国家自然科学基金资助项目(51565023) 云南省教育厅科学研究基金重大专项项目(ZD201504)
【分类号】：TB383.4;TG386.3
【正文快照】： 泡沫金属作为一种新型工程材料,因其密度小、吸能性和吸声性好、热导率低等特性而被广泛应用。泡沫金属的强度较低,一般会作为夹层与致密金属板组成夹层板来使用,这就在充分利用其特性的前提下解决了其强度低的问题。泡沫金属的多孔结构在受压缩时能够吸收大量的能量,因此泡沫

【相似文献】

相关期刊论文 前5条

1 贺永;傅建中;徐月同;陈子辰;;微热压印成型过程缺陷研究[J];浙江大学学报(工学版);2009年01期

2 贺永;傅建中;陈子辰;;微热压印过程中聚合物流动形貌的研究[J];光学精密工程;2008年02期

3 叶向东;丁玉成;;基于聚合物模板的变种压印工艺研究[J];机械工程学报;2012年19期

4 孙国良;王海容;高鲜妮;周志涛;蒋庄德;;TiN模板热压印中的若干关键影响因素仿真分析[J];机械强度;2011年02期

5 蒋梦琳;林仕伟;;纳米热压印聚合物材料的研究进展[J];高分子材料科学与工程;2013年04期

相关博士学位论文 前1条

1 石刚;边缘压印技术在制备功能材料图案中的应用[D];吉林大学;2012年

相关硕士学位论文 前4条

1 马玉辉;聚合物超声波压印成形工艺及优化[D];大连理工大学;2015年

2 徐越;新型微纳米热压印系统及其应用研究[D];浙江大学;2016年

3 邹业兵;卷对卷紫外微纳压印超疏水薄膜的技术及装置研究[D];浙江大学;2017年

4 林澄;皮秒激光制备大面积金属类荷叶结构及其超疏水压印研究[D];清华大学;2014年

，

本文编号：1396362