面向热界面应用的多壁碳纳米管阵列生长优化

发布时间：2018-02-03 15:14

本文关键词： 热界面材料多壁碳纳米管阵列浮动催化化学气相沉积拉曼光谱　出处：《工程热物理学报》2017年06期 　论文类型：期刊论文

【摘要】：由于杰出的导热和柔韧性能,碳纳米管被认为是提升大功率微电子系统热耗散性能的理想热界面材料。多壁碳纳米管阵列能实现低成本的大规模生产,成为制备热界面材料的最佳选择。但是多壁碳纳米管阵列的生长过程的最优因素尚未廓清。本文从实验上系统研究了催化剂的升华温度对浮动催化化学气相沉积法制备出的多壁碳纳米管阵列结构及热输运的影响规律,得到了最佳的催化剂升华温度,为实现最优导热性能的多壁碳纳米管阵列热界面材料提供实验指导。
[Abstract]:Because of its excellent thermal conductivity and flexibility, carbon nanotubes (CNTs) are considered to be ideal thermal interface materials for improving the thermal dissipation performance of high-power microelectronic systems. Multi-walled CNTs arrays can achieve low-cost large-scale production. It is the best choice to prepare thermal interface materials, but the optimal factors for the growth process of multi-walled carbon nanotube arrays have not been clarified. The effect of catalyst sublimation temperature on floating catalytic chemical vapor deposition has been systematically studied in this paper. The structure of multi-walled carbon nanotube array and the influence of thermal transport were investigated. The optimal sublimation temperature of the catalyst is obtained, which provides experimental guidance for the thermal interface material of multi-walled carbon nanotube arrays with optimal thermal conductivity.
【作者单位】：北京科技大学能源与环境工程学院;北京科技大学冶金工业节能减排北京市重点实验室;弗吉尼亚大学机械与航空航天工程系;
【基金】：国家自然科学基金资助项目(No.51422601;No.51306183) 北京科技大学中央高校基本科研业务费国家留学基金项目(No.201404910084)
【分类号】：TB383.1
【正文快照】： 0引S由于杰出的导热和柔韧性,碳纳米管(Carbon 米管(Double walled carbon nanotube,DWCNT)nanotube,CNT)被认为是一种理想的热界面材和多壁碳纳米管(Multi walled carbon nanotube,料,能帮助大功率微电子集成系统耗散多余的 MWCNT),MWCNT的合成比SWCNT更为方便、热量[141。