铁红对PVC复合材料的阻燃性能影响

发布时间：2018-02-10 06:50

  本文关键词： 铁红 聚磷酸铵 PVC 无卤阻燃　出处：《消防科学与技术》2017年09期 　论文类型：期刊论文

【摘要】：通过将铁红和聚磷酸铵(APP)复配后加入到PVC中制备阻燃PVC复合材料,研究此阻燃体系对阻燃PVC复合材料的阻燃性能的影响。通过锥形量热仪、氧指数、扫描电镜等表征手段研究铁红和聚磷酸铵的复配量对PVC阻燃性能的影响,结果表明:当铁红∶APP∶PVC的配比为5%∶25%∶70%时,阻燃PVC复合材料的阻燃性能最佳,其总热释放量、总烟释放量降低,氧指数升高。铁红的添加可以有效改善形成炭层的表明光滑度和致密度,提升PVC复合材料的阻燃性能。
[Abstract]:The flame retardant PVC composites were prepared by adding iron red and ammonium polyphosphate (app) into PVC to study the effect of the flame retardant system on the flame retardant properties of PVC composites. The effects of the mixture of iron red and ammonium polyphosphate on the flame retardancy of PVC were studied by SEM. The results showed that when the ratio of iron red to PVC was 5: 25: 70%, the flame retardant PVC composite had the best flame retardant property and its total heat release was the best. The total smoke emission decreased and the oxygen index increased. The addition of iron red could effectively improve the smoothness and density of the carbon layer and improve the flame retardancy of PVC composites.
【作者单位】： 怀化市消防支队;
【分类号】：TB33

【相似文献】

相关期刊论文 前10条

1 赵永生;王克俭;朱复华;薛平;包文春;赵雁鸣;;蒙脱土/硅烷改性木粉/PVC复合材料[J];复合材料学报;2007年03期

2 李春霞;沈梅;辛振祥;;杜仲翅果壳粉/PVC复合材料力学性能研究[J];塑料包装;2014年03期

3 王平华;王贺宜;唐龙祥;张斌;程文超;梁永标;;碳纳米管/PVC复合材料的制备及表征[J];高分子材料科学与工程;2008年01期

4 张玲;牛建华;孙水升;;纳米CaCO_3的接枝改性及其填充PVC复合材料的性能[J];聚氯乙烯;2008年08期

5 魏守左,陈延勇,严瑞芳;以杜仲胶渣作填料的PVC复合材料的研究[J];材料科学进展;1988年01期

6 曾晓飞,陈建峰,赵红英;纳米CaCO_3-PVC复合材料微观结构和力学性能研究[J];北京化工大学学报(自然科学版);2001年04期

7 叶林忠，郑鲁光，，赵连军，吴其晔;短玻璃纤维/R─PVC复合材料的红外光谱和声发射分析[J];青岛化工学院学报;1995年03期

8 曾晓飞,陈建峰,王国全;纳米CaCO_3/PVC复合材料结构形态与冲击性能[J];高校化学工程学报;2002年02期

9 孙水升,李春忠,张玲,曹宏明;CPE对纳米CaCO_3增韧PVC复合材料界面和性能的影响[J];过程工程学报;2005年05期

10 董鹏飞;韩婧;邵启伟;成荣明;;ZnO纳米棒/PVC复合材料的光催化性能研究[J];华东师范大学学报(自然科学版);2009年05期

相关博士学位论文 前1条

1 岳小鹏;木质素在PVC复合材料中的应用研究[D];华南理工大学;2011年

相关硕士学位论文 前2条

1 万正龙;竹粉/PVC复合材料的制备及性能研究[D];华中农业大学;2010年

2 刘建超;疏水聚磷酸铵及耐水IFR-PP复合材料性能研究[D];东北林业大学;2015年

本文编号：1499915