不同方法制备的球形铸造碳化钨粉末的性能研究

发布时间：2018-02-24 02:03

  本文关键词： 球形铸造碳化钨粉末 等离子旋转电极雾化 显微硬度　出处：《粉末冶金工业》2017年04期 　论文类型：期刊论文

【摘要】：球形铸造碳化钨粉末是一种新型的超耐磨陶瓷颗粒材料,对比研究了不同方法制备的球形铸造碳化钨粉末的化学成分、显微形貌、微观组织、相结构、显微硬度、流动性以及松装密度等特性。结果表明:相对等离子重熔球化法和感应重熔球化法而言,等离子旋转电极雾化法制备的球形铸造碳化钨的总碳含量与共晶碳含量理论值的偏差最小、游离碳和杂质含量最低;粉末颗粒内部更致密、共晶组织更细密、显微硬度最高。感应重熔球化方法制得的粉末流动性最好、松装密度最大。
[Abstract]:The spherical cast tungsten carbide powder is a new type of ultra-wear-resistant ceramic particle material. The chemical composition, microstructure, phase structure and microhardness of the spherical cast tungsten carbide powder prepared by different methods were studied. The results show that compared with plasma remelting spheroidization and induction remelting spheroidization, The total carbon content of spherical cast tungsten carbide prepared by plasma rotating electrode atomization method is the least deviation from the theoretical value of eutectic carbon content, the content of free carbon and impurity is the lowest, the powder particle is denser and the eutectic structure is finer. The best powder fluidity and loose density were obtained by induction remelting spheroidization.
【作者单位】： 广东省科学院广东省材料与加工研究所;
【基金】：国家国际科技合作专项(2011DFR50740) 广东省战略性新兴产业核心技术攻关专项(2011A091102007) 广州市科技计划项目(2012J5100050) 广东省科学院科研平台环境与能力建设专项(2016GDASPT-0209)
【分类号】：TB383.3;TQ136.13

【相似文献】

相关期刊论文 前10条

1 李玉玺;贺跃辉;陈楚轩;戴煜;;铸造碳化钨球形化处理技术的研究[J];中国钨业;2006年04期

2 李玉玺;贺跃辉;陈楚轩;;球形铸造碳化钨的制备技术[J];粉末冶金材料科学与工程;2006年06期

3 黄汝清;李祖来;山泉;蒋业华;周荣;隋育栋;;钢、铁基复合材料中铸造碳化钨颗粒的分解过程[J];特种铸造及有色合金;2012年02期

4 姚继有;绞刀堆焊铸造碳化钨合金新技术[J];中国建材;1984年02期

5 佘建芳;球形铸造碳化钨硬面材料生产新方法[J];硬质合金;1998年04期

6 ;高耐磨材料—铸造碳化钨[J];甘蔗糖业;1978年02期

7 陈平,梁静,伍伟东;铸造碳化钨中总碳的测定[J];现代商检科技;1998年05期

8 陈平,梁静,伍伟东;铸造碳化钨中总碳测定的研究[J];广东有色金属学报;1999年02期

9 宋欢，张松，，张树生，隋全明;铸造碳化钨硬质合金粉末预成形块火焰喷焊工艺及耐磨性的研究[J];粉末冶金技术;1995年04期

10 汤小文,黄本生,杨眉,王子瑜;钻头齿面堆焊用硬质合金耐磨性试验[J];西南石油学院学报;1999年03期

相关硕士学位论文 前2条

1 张宝军;铸造碳化钨/镍基钎料合金复合钎涂材料制备与性能研究[D];长安大学;2007年

2 周庆军;铸造碳化钨颗粒增强铜基复合材料的研究[D];长安大学;2002年

本文编号：1528450