发布时间：2018-02-24 14:34

  本文关键词： 电子束辐照 羧基丁腈橡胶(XNBR) 可膨胀石墨(EG) 纳米石墨片(GnPs) 复合材料　出处：《复合材料学报》2017年05期 　论文类型：期刊论文

【摘要】：利用电子束辐照法制备纳米石墨片(GnPs)-羧基丁腈橡胶(XNBR)复合材料,研究辐射剂量对胶乳共混体系稳定性的影响,并对GnPs-XNBR复合材料的交联度、热稳定性、电性能及其形貌予以表征。结果表明:辐照后GnPs-XNBR复合材料的交联度、热稳定性和体积电阻率提高,而共混乳液的稳定性显著降低。辐照强化了乳胶粒子与石墨片之间的界面结合,形成胶乳粒子包覆石墨片的核-壳结构,进而提高石墨片在基体中分散均匀性,并使GnPs-XNBR复合材料的热稳定性和介电常数提高,导电性和介电损耗降低。
[Abstract]:Nano-graphite flake / carboxylic acrylonitrile-butadiene rubber (NBR) composites were prepared by electron beam irradiation. The effects of radiation dose on the stability of latex blends were studied, and the crosslinking degree and thermal stability of GnPs-XNBR composites were also studied. The results show that the crosslinking degree, thermal stability and volume resistivity of irradiated GnPs-XNBR composites are improved. However, the stability of the blend emulsion was significantly decreased. Irradiation strengthened the interface between latex particles and graphite sheets, formed the core-shell structure of latex particles coated with graphite, and improved the dispersion uniformity of graphite sheets in the matrix. The thermal stability and dielectric constant of GnPs-XNBR composites were improved, and the conductivity and dielectric loss were decreased.
【作者单位】： 黑龙江省科学院技术物理研究所;黑龙江省科学院高技术研究院;
【分类号】：TB332

【相似文献】

相关期刊论文 前5条

1 马蕊然,宁荣昌,阁铜丰;复合材料用环氧树脂的韧化——(七)端羧基丁腈橡胶/双酚-A型环氧树脂/2-乙基-4-甲基咪唑体系的研究[J];玻璃钢/复合材料;1986年S1期

2 吕生华,吕庆强,杨权荣;液体端羧基丁腈橡胶改性氰酸酯/玻璃纤维复合材料的性能研究[J];中国塑料;2005年03期

3 马蕊然;马满珍;潘顺清;;复合材料用环氧树脂的韧化(一)无规羧基丁腈橡胶/双酚A型环氧树脂/-乙基-4-甲基咪唑体系的研究[J];航空材料;1981年02期

4 马蕊然,马满珍,潘顺清;复合材料用环氧树脂的韧化——(一)无规羧基丁腈橡胶/双酚A型环氧树脂/-乙基-4-甲基咪唑体系的研究[J];航空材料;1981年S2期

5 ;[J];;年期

相关博士学位论文 前1条

1 滕谋勇;聚乙烯/明胶、羧基丁腈橡胶/明胶反应增容共混改性研究[D];北京化工大学;2004年

，

本文编号：1530600