磷酸铝-聚醚砜层状复合材料的隔热及介电性能

发布时间：2018-03-12 09:55

  本文选题：聚醚砜　切入点：磷酸铝　出处：《复合材料学报》2017年09期 　论文类型：期刊论文

【摘要】：采用高温煅烧成型工艺在聚醚砜(PES)基体表面复合了AlPO4耐热层,制备得到了AlPO4-PES层状复合材料。利用SEM、激光共聚焦显微镜三维形貌分析(CLSM-3D)、FTIR和TGA等分析技术对AlPO4-PES微观结构、化学成分以及热稳定性进行了表征。研究了AlPO4含量对AlPO4-PES层状复合材料的热导率和介电性能的影响。结果表明:AlPO4层显著地改变了PES基体的微观结构,二者之间通过物理方式紧密结合;随着AlPO4含量的增加,AlPO4-PES层状复合材料的热稳定性明显增强,而热导率却不断降低;AlPO4-PES层状复合材料的介电常数和介电损耗均随着AlPO4含量的增加而减小,并且在0.1~5MHz测试范围内表现出良好的频率稳定性。
[Abstract]:AlPO4 laminated composites were prepared by high temperature calcination process on the surface of polyethersulfone (PES) substrate. The microstructure of AlPO4-PES was analyzed by means of SEM, laser confocal microscopy, 3D FTIR and TGA techniques. The effects of AlPO4 content on the thermal conductivity and dielectric properties of AlPO4-PES laminated composites were investigated. The results showed that the microstructure of PES matrix was significantly changed by the w / AlPO4 layer. The thermal stability of AlPO4-PES laminated composites increased with the increase of AlPO4 content. The dielectric constant and dielectric loss of AlPO4-PES laminated composites decrease with the increase of AlPO4 content, and show good frequency stability in the range of 0.1 ~ 5MHz.
【作者单位】： 燕山大学机械工程学院;燕山大学自润滑关节轴承共性技术航空科技重点实验室;
【基金】：河北省重大科技成果转化专项项目-海上溢油应急清理成套装备(16043303Z)
【分类号】：TB332

【相似文献】

相关期刊论文 前10条

1 袁鸽成,杨安宸,娄燕雄;Al-Sn-Si/Al/steel层状复合材料的变形复合行为及机理[J];机械工程材料;2002年10期

2 徐涛;;金属层状复合材料的发展与应用[J];轻合金加工技术;2012年06期

3 戴耀,刘海现,崔建国,何家文;用最大正应力法则确定层状复合材料中疲劳裂纹的扩展方向[J];兵工学报;2000年S1期

4 彭大暑,刘浪飞,朱旭霞;金属层状复合材料的研究状况与展望[J];材料导报;2000年04期

5 李献民,崔建忠,胡宗式,李梅,陈东琴;金属层状复合材料的超塑变形行为[J];材料导报;2000年08期

6 王国宏;金属-玻璃层状复合材料的发展前景[J];稀有金属快报;2002年02期

7 邵红红,程晓农,陈光;仿生层状复合材料研究概况[J];材料导报;2002年04期

8 昝青峰,汪长安,黄勇,李翠伟,赵世柯;Al_2O_3/Ti_3SiC_2层状复合材料的制备与性能[J];材料工程;2003年09期

9 王国宏;论层状复合材料性能稳定性的提高[J];钛工业进展;2003年06期

10 关春龙;赫晓东;李W，

本文编号：1601062