木粉对聚乳酸流变、结晶及发泡行为的影响

发布时间：2018-03-26 05:23

  本文选题：聚乳酸　切入点：木粉　出处：《高分子材料科学与工程》2017年08期

【摘要】：以超临界CO_2为发泡剂,设计高温保压、低温快速泄压发泡的工艺,制备微孔发泡木粉/聚乳酸复合材料。利用X射线衍射仪、差示扫描量热仪、旋转流变仪对复合体系结晶及流变性能进行分析。采用排水法及扫描电镜研究了木粉含量对发泡材料表观密度、发泡倍率,泡孔密度及泡孔形貌的影响。结果表明,木粉的加入提高了木粉/聚乳酸复合材料熔体的复数黏度和储能模量,降低了聚乳酸的结晶度,提高了泡孔密度,减小了泡孔尺寸。当木粉含量为20%时,木粉/聚乳酸发泡材料表观密度为0.19g/cm~3,发泡倍率达到7倍,泡孔密度为7.23×10~8 cm~(-3),平均泡孔直径为20μm。
[Abstract]:The microporous foamed wood powder / polylactic acid composite was prepared by using supercritical CO_2 as foaming agent, and the technology of high temperature pressure preservation and low temperature rapid pressure releasing foaming was designed. X-ray diffractometer and differential scanning calorimeter (DSC) were used to prepare the microporous foamed wood powder / polylactic acid composite. The effects of wood powder content on the apparent density, foaming ratio, bubble density and morphology of foamed materials were studied by means of drainage and SEM. The addition of wood flour increased the complex viscosity and energy storage modulus of wood flour / polylactic acid composite melt, decreased the crystallinity of polylactic acid, increased the cell density and reduced the pore size. The apparent density of wood powder / polylactic acid foaming material is 0.19 g / cm ~ (-3), the foaming ratio is 7 times, the cell density is 7.23 脳 10 ~ (8) cm ~ (-1) ~ (-3), and the average diameter of foam is 20 渭 m.
【作者单位】： 东北林业大学生物质材料科学与技术教育部重点实验室;
【基金】：中央高校基本科研业务费专项资金项目资助(2572017CB15) 省留学归国人员科学基金(LC2015011) 中国博士后科学基金特别资助(2014T70303)
【分类号】：O633.14;TB332

【相似文献】

相关期刊论文 前5条

1 杨长生,蒋登高,石晓华,蒋雪根;木粉聚醚的流变特性以及粘流温度效应[J];高校化学工程学报;2001年01期

2 苏仕芸,马晓茜,赵增立,李海滨;天然气与木粉共燃过程NO_x生成特性的分析[J];煤气与热力;2003年09期

3 王福安，蒋元力，李雷，王毅红，，蒋登高;木粉聚醚的流变性研究[J];石油化工;1995年04期

4 李思良,曾湘云,刘希凡;木粉填充PP的力学性能[J];中国塑料;1998年04期

5 蒋雪根,杨长生,程建书,蒋登高;木粉聚醚分子量测定及结构分析[J];郑州工业大学学报;2000年04期

相关硕士学位论文 前2条

1 杨瑶;多微孔苄基化改性木粉的制备及其对废水中Cu~(2+)、Pb~(2+)和Zn~(2+)的吸附性能研究[D];中南林业科技大学;2016年

2 杨林峰;基于木粉碱溶体系的木质素分离及结构表征[D];南京林业大学;2013年

本文编号：1666518