中空纤维型自修复复合材料的修复效率及力学性能

发布时间：2018-03-28 03:25

  本文选题：中空纤维型自修复　切入点：复合材料　出处：《宇航材料工艺》2017年04期

【摘要】：以5-亚乙基-2-降冰片烯(ENB)和Grubbs催化剂组成的修复系统为修复剂、以外径为Ф0.9mm的中空玻璃管为载体,通过压力破坏实验和三点弯曲实验研究含有中空玻璃管复合材料的弯曲性能及自修复的效率。结果表明:压力破坏实验给试件带来的损伤程度最大可达到14.67%;已受损的试件在修复系统的作用下,试件的强度能恢复到原强度的99.15%。
[Abstract]:The repair system composed of 5-ethyl-2-norbornene (ENB) and Grubbs catalyst was used as the repair agent, and the hollow glass tube with outer diameter as 0.9mm was used as the carrier. The bending properties and self-repairing efficiency of composite material containing hollow glass tube were studied by pressure failure test and three-point bending test. The results show that the damage degree of the specimen caused by the pressure failure test can reach 14.677.It has been obtained. The damaged specimen is affected by the repair system, The strength of the specimen can be restored to 99.15% of the original strength.
【作者单位】： 天津市现代机电装备技术重点实验室;天津工业大学机械工程学院;
【基金】：国家自然科学基金(11372220)
【分类号】：TB33

【相似文献】

相关期刊论文 前10条

1 李海燕;张丽冰;李杰;王俊;;外援型自修复聚合物材料研究进展[J];化工进展;2014年01期

2 华凌;;“聪明”水凝胶能瞬间实现切口自修复[J];共产党员;2012年08期

3 方征平;羊海棠;徐立华;顾嫒娟;佟立芳;许忠斌;;聚合物基复合材料自修复体系的构成与修复机制分析[J];航空材料学报;2006年03期

4 ;浙大制备成功新型自修复材料[J];化工中间体;2012年06期

5 ;自修复仿生涂层几乎排斥所有液体[J];硅酸盐通报;2011年06期

6 杨长江;陈国需;陈淑莲;赵立涛;廖梓s，

本文编号：1674561