纳米粒子的分散对提高LMPS盐比热容的影响

发布时间：2018-05-06 23:35

  本文选题：太阳能 + 熔盐　； 参考：《太阳能学报》2017年11期

【摘要】：该文在一种新型低熔点四元混合硝酸盐LMPS盐中添加Si O2纳米粒子来提高其比热容。采用超声振荡法和熔融混合法制备纳米LMPS盐,研究2种制备过程对纳米粒子在LMPS盐中分散情况的影响,及纳米粒子的分散对比热容提高的影响。研究表明,在LMPS盐中添加纳米粒子可显著提高LMPS盐的比热容,比热容提高率与纳米粒子在分散均匀程度呈正相关,超声振荡法所制备的纳米LMPS盐比热容提高率高于熔融混合法制备的纳米熔盐。
[Abstract]:In this paper, Sio 2 nanoparticles were added to a new low melting point mixed nitrate LMPS salt to improve its specific heat capacity. Nano-sized LMPS salts were prepared by ultrasonic oscillation method and melt mixing method. The effects of the two preparation processes on the dispersion of nanoparticles in LMPS salts and the effect of dispersion of nanoparticles on the specific heat capacity were studied. The results show that the specific heat capacity of LMPS salt can be significantly increased by adding nano-particles to LMPS salt, and the specific heat capacity increase rate is positively related to the dispersion uniformity of the nanoparticles. The specific heat capacity of nano LMPS prepared by ultrasonic oscillation method is higher than that of nano molten salt prepared by melt mixing method.
【作者单位】： 北京工业大学传热强化与过程节能教育部重点实验室及传热与能源利用北京市重点实验室;
【分类号】：O645.4;TB383.1

【相似文献】

相关会议论文 前4条

1 林卫军;;《研究物质的比热容》教学设计[A];中国当代教育理论文献——第四届中国教育家大会成果汇编（上）[C];2007年

2 曾洪宇;石未凡;陈鏖;;三维量热法比热容测试技术[A];中国化学会第十五届全国化学热力学和热分析学术会议论文摘要[C];2010年

3 苏金瑞;王克勤;屈继锋;朱长飞;;Sm_(0．99)Gd_(0．01)Al_2金属间化合物的声学和比热容性质研究[A];第七届全国内耗学术会议论文集[C];2003年

4 王锋;吴卫东;张纪彦;徐嘉靖;马拥军;吕兵;戴伟;刘强;曹林洪;张继成;葛芳芳;孙卫国;唐永建;;FeAl单晶薄膜的制备及其比热容性能研究[A];第十届中国核靶技术学术交流会摘要集[C];2009年

相关硕士学位论文 前1条

1 朱玉英;过冷状态下熔体比热的研究[D];燕山大学;2003年

，

本文编号：1854418