同时具有高红外辐射率及高电导率的多孔镍镀层

发布时间：2018-05-12 13:40

  本文选题：红外辐射率 + 导电率　； 参考：《功能材料》2017年07期

【摘要】：通过氢气泡模板法制备出了同时具备高电导率和高红外辐射率的多孔镍镀层,满足其在太空中散热以及电磁屏蔽的需要。分析研究了不同沉积时间、氯化铵和氯化镍浓度对多孔镍层孔径和红外发射率的影响。研究结果表明,随着孔洞投影面积比的增加,多孔镍层的红外发射率增加,通过工艺参数的优化,在不影响Ni镀层导电性能的前提下,制备出红外发射率为0.79的多孔镀镍膜层。
[Abstract]:Porous nickel coatings with high conductivity and high infrared emissivity were prepared by hydrogen bubble template method, which can meet the needs of heat dissipation and electromagnetic shielding in space. The effects of different deposition time, concentration of ammonium chloride and nickel chloride on pore size and infrared emissivity of porous nickel layer were studied. The results show that the infrared emissivity of the porous nickel coating increases with the increase of the ratio of the hole projection area. The porous nickel coating with the infrared emissivity of 0.79 is prepared by optimizing the process parameters and without affecting the conductivity of the Ni coating.
【作者单位】： 上海交通大学材料科学与工程学院;中国航天科技集团公司第八研究院第八O四研究所;中国航天科技集团公司第八研究院一四九厂;江苏中翼汽车新材料科技有限公司;
【基金】：国家自然科学基金资助项目(51371116) 航天先进技术联合研究中心技术创新资助项目(USCAST2013-23) 江苏省科技成果转化资助项目(BA2016039)
【分类号】：TB306

【相似文献】

相关期刊论文 前9条

1 黄芸;何伟;许仲梓;张其土;;掺铝氧化锌粉末的制备及其性能研究[J];功能材料;2009年03期

2 张静;黄啸谷;陈娇;张其土;;SmFeO_3的制备及其多波段兼容隐身性能研究[J];功能材料;2011年S1期

3 陈娇;黄啸谷;韩朋德;王丽熙;张其土;;Bi_2O_3/ATO混烧填料的制备及其红外发射率研究[J];功能材料;2011年02期

4 黄啸谷;陈娇;李少炳;王丽熙;张其土;;热处理温度对Bi_2O_3/ATO复合功能填料红外-可见光兼容隐身性能的影响[J];功能材料;2012年15期

5 彭同江;焦永峰;刘海峰;马国华;;ZnO掺杂堇青石基红外陶瓷粉体的研制与表征[J];分析测试学报;2009年06期

6 于洋;于云;张少宗;;NiFe_2O_4红外高辐射涂层的制备及其热物理性能[J];硅酸盐学报;2014年06期

7 何登良;董发勤;刘家琴;王海滨;冯启明;;麦饭石热处理及在远红外基元材料中的应用[J];功能材料;2007年09期

8 何登良;董发勤;刘家琴;王海滨;罗娅君;;麦饭石基铝系远红外基元材料的制备及应用[J];功能材料;2010年03期

9 ;[J];;年期

相关硕士学位论文 前4条

1 熊里;煤矸石—黑滑石—铝矾土制备低膨胀高红外瓷质卫生陶瓷的初步研究[D];景德镇陶瓷学院;2013年

2 董丽娜;粉煤灰质高红外辐射率卫生陶瓷的研制[D];景德镇陶瓷学院;2011年

3 刘芸芸;大气等离子喷涂法制备高温高红外辐射率陶瓷涂层[D];武汉理工大学;2014年

4 许刚科;燃油活化及助燃功能复合材料研究[D];河北工业大学;2006年

，

本文编号：1878829