UV辐射麻纤维复合材料的耐老化性能的研究

发布时间：2018-07-20 08:57

【摘要】：研究了麻纤维增强不饱和聚酯复合材料的耐老化性能。紫外线(UV)辐射和冷凝循环加UV辐照都能导致麻纤维复合物失重,但失重率随延长辐照时间的延长而稳定。同样,UV辐照初期能使麻纤维复合材料的拉伸性能下降,但随时间增长,拉伸性能越来越稳定。同样两类条件下,不同麻纤维复合物拉伸强度和弹性模量的下降都非常相近。但是在水中,麻纤维复合的物的弹性模量比拉伸强度降低更为明显。利用这些条件可以识别这类复合材料是否被水污染。
[Abstract]:The aging resistance of hemp fiber reinforced unsaturated polyester composites was studied. UV radiation and condensation cycle combined with UV irradiation can lead to weight loss of hemp fiber complex, but the weight loss rate is stable with the prolongation of irradiation time. At the beginning of UV irradiation, the tensile properties of hemp fiber composites decreased, but the tensile properties became more and more stable with the increase of time. Under the same two kinds of conditions, the tensile strength and elastic modulus of different flax fiber composites are very similar. But in water, the elastic modulus of hemp fiber composite is more obvious than that of tensile strength. These conditions can be used to identify whether such composites are polluted.
【作者单位】： 湖南工学院材料与化学工程学院;
【基金】：国家自然科学基金项目(21176061) 湖南省重点建设学科(湘教发[2011]76号) 2016年湖南省教育厅重点项目(16A053) 2016年衡阳市科技计划项目(2016KS40) 2016年湖南省教研教改项目(湖南省教育厅湘教通[2016]400号)
【分类号】：TB332

【参考文献】

相关期刊论文 前10条

1 邓华;罗峻;杨建;;浅谈海洋用超高分子量聚乙烯纤维人工加速老化的评价方法[J];中国纤检;2016年12期

2 张建;何春霞;唐辉;付菁菁;王敏;;三种植物纤维填充聚乳酸复合材料性能对比[J];工程塑料应用;2016年11期

3 许大蔚;蒋永发;黎杰鹏;吴丁财;符若文;;硅树脂改性不饱和聚酯的表面性质研究[J];热固性树脂;2016年05期

4 朱坤坤;倪爱清;王继辉;;苎麻/玻璃纤维混杂复合材料的老化研究及寿命预测[J];玻璃钢/复合材料;2016年05期

5 聂亚楠;马东阳;王成启;;不饱和聚酯玻璃钢与环氧乙烯基酯玻璃钢耐久性能试验研究[J];玻璃钢/复合材料;2015年11期

6 杨越飞;徐建锋;赖佳佳;郑峰;宋剑斌;杨文斌;;玄武岩纤维改进亚麻纤维/不饱和聚酯复合材料的耐候性[J];农业工程学报;2015年08期

7 龙洪生;薛平;丁筠;刘新阳;;废弃天然纤维增强高密度聚乙烯复合材料性能研究[J];中国塑料;2014年11期

8 闫冬雪;戢觅之;王柯;傅强;;可降解型聚丁二酸丁二醇酯/聚乳酸原位成纤增强复合材料[J];高分子材料科学与工程;2014年02期

9 杜红伟;;纤维复合材料加固混凝土构件耐久性设计[J];南阳理工学院学报;2012年04期

10 芦长椿;;国内外天然纤维增强复合材料的技术进展[J];纺织导报;2011年03期

【共引文献】

相关期刊论文 前10条

1 李来丙;;UV辐射麻纤维复合材料的耐老化性能的研究[J];化工新型材料;2017年06期

2 张婷婷;董珈豪;韦良强;孙静;黄安荣;秦舒浩;;原位成纤复合材料研究进展[J];塑料科技;2017年06期

3 刘小\，

本文编号：2132983