【摘要】：金属有机骨架(MOFs)是一类新型的多孔纳米材料,由金属团簇和有机配体自组装而成。由于具有超高的表面积、可控的孔尺寸和可调的化学环境等优点,使其在空气净化、化学传感、气体存储、催化和CO2捕捉等方面表现出非常好的应用前景。然而水稳定性一直是阻碍其工业化应用的瓶颈,所以研究MOFs和水的相互作用及MOFs的水解机理具有非常重要的意义。主要从MOFs水稳定性的研究方法,影响因素,如何增强MOFs的抗水性和有关MOFs水稳定性研究的最新动态等方面进行了详细论述,并指出了当前存在的问题和今后的发展方向。
[Abstract]:Organometallic skeleton (MOFs) is a new kind of porous nanomaterials, which is composed of metal clusters and organic ligands. Due to its high surface area, controllable pore size and adjustable chemical environment, it has a promising future in air purification, chemical sensing, gas storage, catalysis and CO2 capture. However, water stability has been the bottleneck of its industrial application, so it is of great significance to study the interaction between MOFs and water and the hydrolysis mechanism of MOFs. In this paper, the research methods, influencing factors, how to enhance the water resistance of MOFs and the latest trends in the study of water stability of MOFs are discussed in detail, and the existing problems and the future development are pointed out.
【作者单位】： 河南工业大学理学院;
【基金】：国家自然科学基金(11304079、11404094、11504088) 国家留学基金(201508410255) 河南省高等学校青年骨干教师(HNQG001316) 河南省省属高校基本科研业务费专项资金资助的课题(2014YWQQ21)
【分类号】：TB383.1

【相似文献】

相关博士学位论文 前2条

1 宗恩敏;锆化炭基复合材料的合成及其对磷酸盐的吸附性能研究[D];南京大学;2013年

2 孙西同;磁性高分子复合材料的制备及对Cr(Ⅵ)的吸附性能研究[D];中国科学院研究生院(过程工程研究所);2015年

相关硕士学位论文 前10条

1 苗晋朋;Cu-BTC@GO复合材料的机械化学合成与成型及其吸附性能研究[D];华南理工大学;2015年

2 李伟平;偕胺肟基—聚丙烯腈/剥离钠基蒙脱石复合材料的合成及对铀的吸附性能研究[D];兰州大学;2015年

3 邢海涛;基于石墨烯复合材料的制备及其对重金属离子的吸附性能研究[D];闽南师范大学;2015年

4 姚蔓莉;介孔氧化硅和介孔炭基纳米材料的制备及其二氧化碳吸附性能研究[D];浙江师范大学;2015年

5 孔童童;氨基功能化多孔材料的制备及其CO_2吸附性能研究[D];青岛科技大学;2016年

6 邢静;系列纳米过渡金属氧化物的制备及其吸附性能研究[D];青岛科技大学;2016年

7 黄虹;二硒化钼及其复合材料的制备和吸附性能研究[D];江苏大学;2016年

8 方贝贝;金属氧化物复合材料的制备及其对有机染料的吸附性能研究[D];吉林大学;2016年

9 王玮;功能纳米复合材料的设计制备及吸附性能研究[D];燕山大学;2016年

10 张旭阳;Cu-MOF/PLA熔喷用复合材料的制备及重金属吸附性能研究[D];浙江理工大学;2017年

，

本文编号：2192413