连续玻璃纤维增强聚氨酯复合材料的力学性能

发布时间：2018-09-10 12:55

【摘要】：为了代替传统的钢制鱼尾板与绝缘部件组成的"机械绝缘接头",通过拉挤成型制备了连续玻璃纤维(GF)质量分数高达70.5%的聚氨酯/玻璃纤维(PUR/GF)复合材料。分别对复合材料在0°和90°方向进行了拉伸、弯曲和压缩性能测试;同时,结合扫描电子显微镜(SEM)观察了拉伸断口,分析了GF在PUR基体中的分布情况及复合材料在拉伸试验中的断裂机理。研究结果表明,0°方向的拉伸强度、弯曲强度以及压缩强度都有很明显的提高,且均符合钢轨鱼尾板的强度标准。
[Abstract]:In order to replace the traditional "mechanical insulating joint" of steel fish-plate and insulating parts, polyurethane / glass fiber (PUR/GF) composites with continuous glass fiber (GF) content up to 70.5% were prepared by pullout molding. The tensile, bending and compression properties of the composites were tested in the direction of 0 掳and 90 掳, respectively, and the tensile fracture was observed by scanning electron microscope (SEM). The distribution of GF in PUR matrix and the fracture mechanism of composites in tensile test were analyzed. The results show that the tensile strength, bending strength and compression strength in the direction of 0 掳are obviously improved, and all of them accord with the strength standard of the rail fishplate.
【作者单位】： 上海理工大学材料科学与工程学院;上海高铁电气科技有限公司;
【基金】：上海市教委创新项目(NO.1522076) 上海张江国家自主创新示范区专项发展资金重点项目(201505-JD-B108-009)
【分类号】：TB332

【参考文献】

相关期刊论文 前10条

1 赵庆波;赵春丽;冯曼;黄丽;王成忠;;连续玻纤增强聚氨酯树脂复合材料制备及性能研究[J];聚氨酯工业;2016年03期

2 左晓玲;张道海;罗兴;吴斌;郝智;郭建兵;;长玻纤增强复合材料老化研究进展及防老化研究[J];塑料工业;2013年01期

3 韩红青;;聚氨酯胶粘剂的研究及改性现状[J];聚氨酯工业;2012年06期

4 朱长春;翁汉元;吕国会;张俊良;;国内外聚氨酯工业最新发展状况[J];化学推进剂与高分子材料;2012年05期

5 张蔚;陈丰;孙宇;曹春平;;低密度长玻纤增强聚氨酯复合材料的力学性能[J];工程塑料应用;2011年02期

6 李晓明;张义新;冯辉霞;郭静威;李汉峰;;聚氨酯涂料研究现状及发展[J];应用化工;2010年07期

7 郭书良;段跃新;肇研;罗云烽;;连续玻璃纤维增强热塑/热固性复合材料力学性能研究[J];玻璃钢/复合材料;2009年05期

8 许俊强;郭芳;储伟;高炜斌;金学军;吴永;;玻纤增强硬质聚氨酯材料的合成及其力学性能[J];合成化学;2009年02期

9 雷文;卢斌;任超;顾大询;王世明;;高密度聚氨酯硬泡塑料/玻纤粉复合材料的研究[J];聚酯工业;2008年05期

10 宋艳江;章刚;朱鹏;王晓东;黄培;;玻璃纤维改性热塑性聚酰亚胺复合材料弯曲性能(Ⅱ)——高温力学性能[J];南京工业大学学报(自然科学版);2008年03期

【共引文献】

相关期刊论文 前10条

1 李瑶;陆瑜，

本文编号：2234501