竹材酚醇液化树脂为壁材相变微胶囊的制备与表征

发布时间：2018-10-10 12:14

【摘要】：以竹材酚醇液化树脂为壁材,石蜡为芯材,采用原位聚合法制备具有相变储能的微胶囊,研究芯壁比、pH值和乳化剂用量对微胶囊制备和性能的影响,利用扫描电镜、红外光谱、激光粒度仪和同步热分析仪对微胶囊的性能进行表征。结果表明:芯壁为1∶1,pH=5.5,乳化剂用量为10%时,制备的微胶囊性能较好,其相变热焓为83.49J/g,储能率为63.47%,粒径分布范围为4.4~399.4μm;微胶囊质地较硬,不团聚,具有良好的热稳定性,可以用来制备相变储能复合材料。
[Abstract]:Taking bamboo phenol-alcohol liquefaction resin as wall material and paraffin as core material, microcapsules with phase change energy storage were prepared by in-situ polymerization. The effects of core / wall ratio, pH value and emulsifier dosage on the preparation and properties of microcapsules were studied. The properties of microcapsules were characterized by laser granulometer and synchronous thermal analyzer. The results show that when the core wall is 1: 1 ~ 1 ~ (-1) pH ~ (5. 5) and emulsifier dosage is 10, the microcapsules have good properties, the enthalpy of phase transition is 83.49 J / g, the energy storage rate is 63.47, the particle size distribution range is 4.439. 4 渭 m, and the microcapsules are hard, do not reunite, and have good thermal stability. It can be used to prepare phase change energy storage composites.
【作者单位】： 浙江省林业科学研究院;
【基金】：浙江省科技计划项目(2014F50019) 浙江省林业厅省院合作项目(2013SY18) 浙江省公益科技项目(2014C32043)
【分类号】：TB34

【相似文献】

相关期刊论文 前10条

1 李家武;;低温相变储能蜡市场前景广阔[J];河南化工;2014年05期

2 张东,周剑敏,吴科如;相变储能复合材料及其电力调峰功能分析[J];华东电力;2003年09期

3 张东,周剑敏,吴科如;相变储能复合材料的研究和应用[J];节能与环保;2004年01期

4 张东,周剑敏,吴科如,李宗津;颗粒型相变储能复合材料[J];复合材料学报;2004年05期

5 王永川,陈光明,张海峰,洪峰;相变储能材料及其实际应用[J];热力发电;2004年11期

6 王守绪;杜世发;翁晓龙;邓龙江;;环氧树脂-磷酸氢二钠复合相变储能材料的制备与性能研究[J];功能材料;2007年04期

7 郭茶秀;张务军;魏新利;;新型相变储能设备的强化传热研究[J];冶金能源;2008年01期

8 张焘;张东;;无机盐高温相变储能材料的研究进展与应用[J];无机盐工业;2008年04期

9 王彦敏;;相变储能技术在采暖空调领域的应用研究[J];科技资讯;2009年30期

10 赵杰;唐炳涛;张淑芬;杨振宇;贾超;;相变储能材料在工业余热回收中的应用[J];化工进展;2009年S1期

相关会议论文 前10条

1 黄凯良;冯国会;刘馨;;相变储能房间节能技术研究应用进展及拓展潜力[A];全国暖通空调制冷2010年学术年会资料集[C];2010年

2 赵杰;唐炳涛;张淑芬;杨振宇;贾超;;相变储能材料在工业余热回收中的应用[A];中国化工学会2009年年会暨第三届全国石油和化工行业节能节水减排技术论坛会议论文集（上）[C];2009年

3 高U，

本文编号：2261727