CAB对红外低发射率涂层性能的优化研究

发布时间：2019-07-14 18:56

【摘要】：为了优化原有红外低发射率涂层的性能,向红外低发射率涂层中加入醋酸丁酸纤维素(CAB),并对涂层进行红外发射率(8~14?m)、扫描电子显微镜(SEM)、力学性能及耐盐水性能测试。结果表明:加入醋酸丁酸纤维素可以促使涂层中铝粉定向排列并形成"镜面"结构,同时减少了涂层的表面缺陷,从而保证涂层发射率基本不变的情况下降低原有涂层的铝粉含量(由40%降低到30%),且优化后的涂层力学性能及耐盐水性能都优于原有涂层。
[Abstract]:In order to optimize the performance of the original infrared low emissivity coating, cellulose acetate(CAB)was added to the infrared low emissivity coating. The results show that adding cellulose acetate butyrate can promote the orientation of aluminum powder in the coating and form the``mirror'' structure, and reduce the surface defects of the coating, so as to ensure that the aluminum powder content of the original coating is reduced(reduced from 40%to 30%)under the condition that the emissivity of the coating is basically unchanged, and the optimized mechanical properties and salt resistance of the coating are better than that of the original coating.
【作者单位】： 南京航空航天大学材料科学与技术学院;江苏协同创新中心;
【基金】：江苏高校优势学科建设工程资助项目 国家自然科学基金项目(51403102) 江苏省自然科学基金项目(BK20140811)
【分类号】：TB306

【相似文献】

相关期刊论文 前10条

1 邓照西;冷一欣;蒋彩云;;醋酸丁酸纤维素合成研究[J];化学研究与应用;2008年04期

2 蒋彩云;黄春香;邓照西;冷一欣;;醋酸丁酸纤维素的酯化及动力学[J];江苏工业学院学报;2009年01期

3 曹妍;李会泉;张军;何嘉松;张懿;;醋酸丁酸纤维素在离子液体中的均相合成[J];化工学报;2009年07期

4 杨武;鲁文杰;赵磊;;增塑性光固化醋酸丁酸纤维素酯的合成与应用[J];中国涂料;2010年05期

5 杨武;鲁文杰;赵磊;;增塑性光固化醋酸丁酸纤维素酯的合成与应用[J];广东化工;2010年04期

6 陈明光,周韬;浅谈醋酸丁酸纤维素在木材淙料中的应用[J];中国涂料;1997年01期

7 黄彩结;张容丽;姜玉;廖兵;庞浩;;醋酸丁酸纤维素的非均相合成法[J];涂料工业;2008年06期

8 刘继泉;宋磊;;高丁酰基含量醋酸丁酸纤维素的生产[J];当代化工;2008年04期

9 ;江苏如皋年产1万吨醋酸丁酸纤维素等项目[J];乙醛醋酸化工;2014年04期

10 柴多里;张小翠;崔庆飞;;微波辅助合成醋酸丁酸纤维素的研究[J];广州化工;2011年15期

相关硕士学位论文 前2条

1 谭卓华;醋酸丁酸纤维素的改性研究[D];广东工业大学;2008年

2 刘芬;聚乙烯醇/醋酸丁酸纤维素电纺芯/壳纤维氧四环素控制释放的研究[D];湖北大学;2011年

，

本文编号：2514448