基于正交设计的模型试验相似材料的配比试验研究

Research on similar material proportioning test of model test based on orthogonal design

[1] [2] [3] [4] [5]

DONG Jin-yu,YANG Ji-hong,YANG Guo-xiang,WU Fa-quan,LIU Hong-shuai（1.North China University of Water Resources and Electric Power,Zhengzhou 450011,China;2.Key Laboratory of Engineering

[1]华北水利水电学院,河南郑州450011; [2]中国科学院地质与地球物理研究所中国科学院工程地质力学重点实验室,北京100029; [3]中国地震局工程力学所,黑龙江哈尔滨150080

文章摘要：在前人相似材料研究的基础上,应用正交设计方法,以（铁粉＋重晶石粉）/骨料、铁粉/（铁粉＋重晶石粉）、黏结剂浓度、石膏含量为4个因素,每个因素设置5个水平,设计了25组材料配比方案,进行了称重、单轴压缩、劈裂和直剪试验,获得了不同配比相似材料的密度、抗压强度、抗拉强度、弹性模量、泊松比、内摩擦角和黏聚力等物理力学性质指标。试验结果表明：不同配比相似材料的物理力学参数分布的范围较大,能够满足不同性质岩体模型试验对岩体相似材料的要求;采用极差分析法分析了各因素的敏感性,发现（铁粉＋重晶石粉）/骨料对试件密度、内摩擦角起主要控制作用,黏结剂浓度对试件的抗压强度、抗拉强度、弹性模量、黏聚力起主要控制作用;并作出了各因素对相似材料物理力学参数影响的直观分析图,分析了各因素对相似材料参数的影响规律。

Abstr：On the basis of previous research of similar material,the weight ratio of iron ore powder plus barite powder to aggregates,the weight ratio of iron ore powder to iron ore powder plus barite powder,adhesive concentration and gypsum content were selected as four factors,and every factor had five variable levels.According to twenty five schemes of material mixture ratio designed by orthogonal design method,laboratory uniaxial compression test,split test and direct shear test were conducted.Physical and mechanical indexes of similar material such as unit weight,compressive strength,tensile strength,elastic modulus,poisson ratio,internal friction angle and cohesion were obtained under different material mixture ratios.The tests results show that physical and mechanical indexes of similar material vary in a large range and can meet the needs for rock similar material in different physical model test of rock slope.The sensitivity of every factor was analyzed by using extremum difference method.The results show that the weight ratio of iron ore powder plus barite powder to aggregates has control effect on density and internal friction angle of the specimen,and adhesive concentration has control effect on compressive strength,tensile strength,elastic modulus and cohesion of the specimen.The relationship between factors and parameters of similar material were studied by direct analysis charts of the factors affecting physical and mechanical indexes of the material.

文章关键词：

Keyword：:orthogonal design method similar material extremum difference analysis sensitivity direct analysis chart

课题项目：国家自然科学基金青年基金资助项目（40702055）; 汶川地震地质灾害调查评价资助项目（1212010914029）; 华北水利水电学院高层次人才引进项目

作者信息：会员可见

  本文关键词：基于正交设计的模型试验相似材料的配比试验研究，由笔耕文化传播整理发布。