冰晶石熔盐介质中铝热还原-熔盐电解二氧化硅

发布时间：2018-08-11 12:02

【摘要】：讨论了铝热还原二氧化硅的热力学条件,热力学计算结果表明铝热还原二氧化硅的反应在热力学上可行.差示扫描量热法分析结果表明,铝热还原二氧化硅反应的表观活化能为697.5 k J/mol,反应级数为3.7.在冰晶石熔盐介质中铝热还原二氧化硅,可得到含8.56%硅的铝硅合金及富氧化铝的冰晶石熔盐;使用惰性阳极电解分离后的富氧化铝的冰晶石熔盐,可得到含94.01%铝的铝硅合金及氧气,硅的回收率为83.43%.
[Abstract]:The thermodynamic conditions of aluminothermic reduction of silica are discussed. The results of thermodynamic calculation show that the reaction of aluminothermic reduction of silica is feasible in thermodynamics. The results of differential scanning calorimetry show that the apparent activation energy of the aluminothermic reduction of silica is 697.5 kJ / mol and the reaction order is 3.7. Aluminum-silicon alloy containing 8.56% silicon and cryolite molten salt rich in alumina can be obtained by aluminothermic reduction of silica in cryolite molten salt medium, and cryolite molten salt rich in alumina can be separated by inert anode electrolysis. Al-Si alloy and oxygen containing 94.01% Al were obtained. The recovery rate of Si was 83.43.
【作者单位】： 东北大学冶金学院;
【基金】：国家自然科学基金资助项目(51322406) 教育部新世纪优秀人才支持计划项目(NCET-13-0107) 中央高校基本科研业务费专项资金资助项目(N140205001;L1502014)
【分类号】：TF821;TN304.12

【相似文献】

相关期刊论文 前10条

1 J.LANGLAIS,R.HARRIS,沈千碧;用铝热还原法提取锶[J];四川有色金属;1997年02期

2 张明杰,李继东,郭清富;真空铝热还原法生产金属锶——铝热还原工艺的研究[J];东北大学学报;2004年12期

3 聂建华;李亚伟;甘明亮;李远兵;颜浩;;还原气氛下铝热还原法合成TiN-Al_2O_3复合材料[J];耐火材料;2007年04期

4 邹兴武;王树轩;杨占寿;王舒娅;祁米香;;真空铝热还原法制备金属锶工艺研究[J];盐湖研究;2012年03期

5 王耀武;彭建平;狄跃忠;冯乃祥;李猛;;以菱镁石为原料铝热还原炼镁的实验研究[J];真空科学与技术学报;2013年07期

6 张淑芬，李平，杜富英，，路连清;铝热还原法制备稀土－铝合金[J];稀土;1994年04期

7 于金,蒋建清,方峰,董岩,谈荣生,吴三械;真空铝热还原法制备金属Sr的热力学分析及实验研究[J];金属学报;2005年08期

8 王耀武;尤晶;冯乃祥;胡文鑫;;CaF_2在真空铝热还原炼镁过程中的行为研究[J];真空科学与技术学报;2012年10期

9 王才明,肖维超,周丽;铝热还原法生产铌铁合金中影响铌收率的因素分析[J];稀有金属与硬质合金;2005年01期

10 于金;吴三械;董岩;谈荣生;朱鸣芳;;真空铝热还原法制备金属锶的反应机理[J];东南大学学报(自然科学版);2006年06期

相关硕士学位论文 前2条

1 陈宣任;铝热还原氮化微晶白云母的高温物相演变[D];成都理工大学;2010年

2 唐成伟;真空铝热还原炼锂新工艺的研究[D];东北大学;2013年

本文编号：2176938