本体聚合法合成PMMA共聚物及其性能研究

发布时间：2018-01-07 06:24

  本文关键词：本体聚合法合成PMMA共聚物及其性能研究　出处：《华东理工大学》2016年硕士论文　论文类型：学位论文

  更多相关文章： 甲基丙烯酸甲酯 甲基丙烯酸二环戊基酯 本体聚合 耐热性

【摘要】：本文主要针对工业生产过程中PMMA的高温连续本体聚合存在体系粘度高、传热慢、容易产生自加速效应的问题,研究了甲基丙烯酸甲酯(MMA)和甲基丙烯酸二环戊基酯(HDCPMA)的自由基本体共聚合反应,比较了一般聚合温度(80～90℃)和高温(110℃)条件下的共聚合行为的变化,考察了温度对共聚物的结构和性能的影响,最后研究了粘度对丙烯酸酯共聚反应体系的竞聚率和动力学的影响。常温和高温自由基本体聚合反应中,通过NMR、GPC、UV-Vis、DSC及TG等手段对制备的共聚物P(HDCPMA-co-MMA)进行表征分析,考察了单体HDCPMA及反应温度对PMMA共聚物结构及性能的影响,并利用FR法、K-T法和YBR法计算共聚单体的竞聚率。结果表明,HDCPMA显著提高了PMMA共聚物的玻璃化转变温度,改善了耐热性,且不影响其透光率；相对分子量随HDCPMA含量的升高而增大。温度升高,HDCPMA的竞聚率由1.0986减小至0.5460,MMA的竞聚率由2.5343增大至4.3096。升高反应温度,增大了聚合反应速率,HDCPMA的反应速率受温度影响较大。常温本体聚合反应中,体系粘度增大,空间位阻效应明显,HDCPMA的竞聚率由1.0986增大至4.6425,MMA的竞聚率由2.5343减小至2.1132；粘度增大,使聚合反应速率降低。同时,在MMA/MA常温本体共聚合体系,增大粘度,MMA的竞聚率由1.8419减小至1.0734,MA的竞聚率由0.6076减小至0.5022。
[Abstract]:This article mainly aims at the high temperature PMMA in the industrial production process of continuous bulk polymerization system has high viscosity, heat transfer is slow, prone to auto acceleration effect problem of methyl methacrylate (MMA) and dicyclopentanyl methacrylate ester (HDCPMA) by Free Radical Bulk Copolymerization, compared the polymerization temperature (80 to 90 DEG C) and high temperature (110 DEG C) under the condition of copolymerization behavior changes, the effect of temperature on the structure and properties of copolymers were investigated, finally studied the viscosity of acrylate copolymerization reaction system reactivity ratio and dynamics. The effects of normal temperature and high temperature free radical polymerization, by NMR, GPC, UV-Vis, DSC and TG of copolymer prepared by P (HDCPMA-co-MMA) were analyzed, the effects of monomer HDCPMA and reaction temperature on the structure and properties of PMMA copolymers, and the use of FR method, K-T method and YBR method to calculate the comonomer The reactivity ratio of body. The results showed that HDCPMA significantly increased the glass transition temperature of PMMA copolymer, improved heat resistance, and does not affect the light transmittance; relative molecular weight increased with the increase of the content of HDCPMA. Temperature, HDCPMA reactivity ratio decreased from 1.0986 to 0.5460 MMA, the reactivity ratio by 2.5343 increased to 4.3096. the reaction temperature, increasing the rate of polymerization, the reaction rate of HDCPMA is influenced by temperature. At room temperature the bulk polymerization reaction, the viscosity and steric effect, HDCPMA reactivity ratio increased from 1.0986 to 4.6425 MMA, the reactivity ratio decreased from 2.5343 to 2.1132; the increase of viscosity. The polymerization rate is reduced. At the same time, in the MMA/MA room temperature bulk copolymerization system, viscosity and reactivity ratio of MMA decreased from 1.8419 to 1.0734 MA, the reactivity ratio decreased from 0.6076 to 0.5022.

【学位授予单位】：华东理工大学
【学位级别】：硕士
【学位授予年份】：2016
【分类号】：O631.5

【参考文献】

相关期刊论文 前10条

1 刘捷;曹春雷;高天正;于涛;赵爽;张会轩;;通过高温自由基聚合合成耐热聚甲基丙烯酸甲酯树脂[J];高分子材料科学与工程;2015年11期

2 王莉洪;王丹丹;孟晓佳;;国内外PMMA生产和技术现状[J];弹性体;2015年03期

3 李健民;;用高温连续自由基聚合工艺制备丙烯酸树脂——聚合机理、产品性能及应用[J];粘接;2015年06期

4 曹春雷;谭志勇;张子健;张会轩;;链转移剂叔十二烷基硫醇对高温连续本体法合成PMMA热稳定性的影响[J];高分子材料科学与工程;2013年02期

5 陈继新;吕洁;赵金德;胡慧林;刘哲;;聚甲基丙烯酸甲酯(PMMA)生产工艺与设备研究概述[J];化工科技;2012年02期

6 郑成赋;程芳;张建军;解孝林;;氢键对P(MMA—co—MAAM)共聚物T_g的影响[J];华中科技大学学报(自然科学版);2010年02期

7 张丹;谢凤国;王宝军;杨肃宁;包永忠;黄志明;;甲基丙烯酸甲酯本体聚合动力学研究[J];化工生产与技术;2008年04期

8 曹艳霞;李光吉;刘慧民;;新型聚(甲基)丙烯酸酯/盐透明材料的制备及其性能[J];高分子通报;2007年11期

9 刘慧民;李光吉;曹艳霞;;光学树脂用单体甲基丙烯酸双环戊烯酯的合成及聚合[J];塑料工业;2007年05期

10 王朋国;马素德;胡波;钟力生;徐传骧;;连续反应制备聚合物光纤用PMMA芯颗粒料[J];塑料工业;2006年01期

相关会议论文 前2条

1 王综轶;王元清;杜新喜;衡月昆;秦中华;;有机玻璃(亚克力)的力学性能及其工程应用[A];第十五届全国现代结构工程学术研讨会论文集[C];2015年

2 方文;王继辉;孔振兴;;邻苯二甲酸二烯丙酯的高温聚合研究[A];第十七届玻璃钢/复合材料学术年会论文集[C];2008年

相关硕士学位论文 前4条

1 蒋晓磊;窄分子量分布PMMA的连续化制备[D];浙江大学;2013年

2 陈超;甲基丙烯酸丁酯高温本体均聚及共聚行为研究[D];华东理工大学;2013年

3 田丽娜;特厚有机玻璃生产中MMA本体聚合动力学与传热耦合研究[D];浙江大学;2006年

4 孙东海;N-环己基马来酰亚胺耐热改性PMMA的研究[D];河北大学;2002年

，

本文编号：1391361