桑枝SCMP浆阴离子基团的吸附过程及吸附机理

发布时间：2018-07-11 13:20

  本文选题：阴离子基团 + 亚甲基蓝　； 参考：《化工学报》2017年01期

【摘要】：通过研究桑枝SCMP浆中阴离子基团(AGs)对亚甲基蓝(MB)的吸附性能实验,运用Langmuir等温方程和Freundlich等温方程对桑枝SCMP浆H_2O_2漂白中AGs对亚甲基蓝(MB)的吸附结果进行拟合,表明桑枝SCMP浆对MB的吸附过程更符合Langmuir吸附模型,得出该吸附过程是单分子层吸附与非匀质吸附共存的优惠型吸附;并采用X射线光电子能谱(XPS)分析纸浆中阴离子基团和纸浆表面元素及种类的变化情况。H_2O_2漂白会形成新的SAGs,提高纸浆纤维表面的磺化程度,同时纸浆纤维中木素含量降低,纤维素和半纤维素含量增加。
[Abstract]:The adsorption of methylene blue (MB) by anionic groups (AGs) in mulberry branch SCMP pulp was studied. Langmuir isothermal equation and Freundlich isothermal equation were used to simulate the adsorption of methylene blue (MB) by AGs in H _ 2O _ 2 bleaching of mulberry branch SCMP pulp. The results showed that the adsorption process of MB on mulberry branch SCMP pulp was more consistent with Langmuir adsorption model, and it was concluded that the adsorption process was a preferential adsorption with the coexistence of monolayer adsorption and non-homogeneous adsorption. X ray photoelectron spectroscopy (XPS) was used to analyze the changes of anionic groups and surface elements and types of pulp. H _ 2O _ 2 _ 2 bleaching will result in the formation of new SAGs, and increase the degree of sulfonation on the surface of pulp fibers, and decrease the lignin content in pulp fibers. The content of cellulose and hemicellulose increased.
【作者单位】： 广西大学轻工与食品工程学院;广西清洁化制浆造纸与污染控制重点实验室;
【基金】：广西自然科学基金项目(2015GXNSFBA139038) 广西清洁化制浆造纸与污染控制重点实验室项目(2013GXNSFFA019005)
【分类号】：TS745;O647.3

【相似文献】

相关期刊论文 前2条

1 郭范,傅佩珍,王俊新,杨治平,郭卫福,吴以成;CaO-B_2O_3-CO_2-H_2O体系中合成Ca_2B_6O_(11)·H_2O[J];人工晶体学报;2000年S1期

2 ;[J];;年期

相关硕士学位论文 前5条

1 吴峥;杯[4]吡咯化合物的合成及其阴离子识别[D];湖南大学;2008年

2 袁继文;同时结合金属盐阳、阴离子的聚合物—席夫碱双功能配位萃取剂的合成及性能研究[D];武汉纺织大学;2011年

3 李蒙蒙;饱和/三缺位Keggin型多酸阴离子功能配合物的控制合成及性能研究[D];河南大学;2013年

4 杨远盛;阴离子粘土合成及吸附砷（V）的研究[D];合肥工业大学;2005年

5 代守龙;Gd~(3+)荧光探针探测C12A7不同笼中阴离子基团变化[D];东北师范大学;2013年

，

本文编号：2115339