Enhancement of post-annealing stability in Co/Ni multilayers
发布时间：2021-11-19 04:16
Enhancement of post-annealing stability in Co/Ni multilayers with perpendicular magnetic anisotropy（PMA） was obtained by inserting Au layers into Ni/Co interfaces.After annealing at 350℃,the effective magnetic anisotropy density(Keff) for Ta（3）/Pt（2）/[Co（0.3）/Ni（0.6）/Au（0.3）]×3/Co（0.3）/Pt（l）/Ta（3）（in nm） keeps at0.48 ×105 J·m-3.Scanning transmission electron microscopy-high-angle annular dark field（STEM-HAADF）analysis shows that the diffusion between N...
【文章来源】：Rare Metals. 2016,35(10)EISCICSCD
【文章页数】：5 页
【文章目录】：
1 Introduction
2 Experimental
3 Results and discussion
4 Conclusion
【参考文献】：
期刊论文
[1]Enhanced methanol oxidation activity of Au@Pd nanoparticles supported on MWCNTs functionalized by MB under ultraviolet irradiation[J]. Ming-Li Xu,Xi-Kun Yang,Ying-Jie Zhang,Shu-Biao Xia,Peng Dong,Guo-Tao Yang. Rare Metals. 2015(01)
[2]Co/Pt multilayer-based pseudo spin valves with perpendicular magnetic anisotropy[J]. Shuai Liu,Guang-Hua Yu,Mei-Yin Yang,Hai-Lang Ju,Bao-He Li,Xiao-Bai Chen. Rare Metals. 2014(06)
[3]Electronic structures of Heusler alloy Co2FeAl1-xSix surface[J]. XU Xiaoguang, ZHANG Delin, WU Yong, ZHANG Xin, LI Xiaoqi, YANG Hailing, and JIANG Yong State Key Laboratory for Advanced Metals and Materials, School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China. Rare Metals. 2012(02)
本文编号：3504270
【文章来源】：Rare Metals. 2016,35(10)EISCICSCD
【文章页数】：5 页
【文章目录】：
1 Introduction
2 Experimental
3 Results and discussion
4 Conclusion
【参考文献】：
期刊论文
[1]Enhanced methanol oxidation activity of Au@Pd nanoparticles supported on MWCNTs functionalized by MB under ultraviolet irradiation[J]. Ming-Li Xu,Xi-Kun Yang,Ying-Jie Zhang,Shu-Biao Xia,Peng Dong,Guo-Tao Yang. Rare Metals. 2015(01)
[2]Co/Pt multilayer-based pseudo spin valves with perpendicular magnetic anisotropy[J]. Shuai Liu,Guang-Hua Yu,Mei-Yin Yang,Hai-Lang Ju,Bao-He Li,Xiao-Bai Chen. Rare Metals. 2014(06)
[3]Electronic structures of Heusler alloy Co2FeAl1-xSix surface[J]. XU Xiaoguang, ZHANG Delin, WU Yong, ZHANG Xin, LI Xiaoqi, YANG Hailing, and JIANG Yong State Key Laboratory for Advanced Metals and Materials, School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China. Rare Metals. 2012(02)
本文编号：3504270
本文链接：https://www.wllwen.com/kejilunwen/jisuanjikexuelunwen/3504270.html