不同浸水时间风干煤样瓦斯吸附解吸规律实验

发布时间：2018-06-17 16:19

  本文选题：浸水时间 + 瓦斯吸附解吸　； 参考：《煤矿安全》2017年12期

【摘要】：为了研究浸水风干煤样瓦斯吸附解吸规律,选择未浸水的原煤样和浸水3、15、30 d风干煤样进行恒温动态瓦斯吸附解吸实验,得到瓦斯累积吸附解吸量随时间变化的实测曲线。对所选煤样进行比表面积及孔径分析,得到其比表面积、孔容和孔径分布。结果表明:浸水风干煤样瓦斯累积吸附量随压力变化的趋势与原煤样一致;浸水风干煤样解吸初始20 min内解吸量倒数与时间函数成线性关系;浸水时间增加,风干煤样的饱和吸附量、比表面积、总孔容、微孔孔容先减小后增大,平均孔径先增大后减小。
[Abstract]:In order to study the law of gas adsorption and desorption of soaking air dry coal samples, the experiment of dynamic gas adsorption and desorption of unsoaked raw coal samples and soaked 3,15,30 D wind dry coal samples was carried out. The measured curves of the cumulative adsorption desorption of gas with time were obtained. The specific surface area and pore size of the selected coal samples were analyzed, and the specific surface area, pore volume and the pore volume were obtained. The results show that the trend of gas accumulation and adsorption with pressure varies with the raw coal, and the inverse number of solution absorption in the initial 20 min desorption is linear with the time function; the soaking time increases, the saturated adsorption capacity of the coal sample is higher than the surface area, the total pore volume, and the micropore Kong Rong decreases first and then increases. The average pore size increases first and then decreases.
【作者单位】： 中国矿业大学(北京)资源与安全工程学院;
【分类号】：TD712

【相似文献】

相关期刊论文 前1条

1 潘俊锋;宁宇;蓝航;彭永伟;夏永学;魏向志;王书文;;基于千秋矿冲击性煤样浸水时间效应的煤层注水方法[J];煤炭学报;2012年S1期

相关博士学位论文 前1条

1 闫发志;基于电破碎效应的脉冲致裂煤体增渗实验研究[D];中国矿业大学;2017年

相关硕士学位论文 前10条

1 周俊义;加载煤样各向异性超声响应特征研究[D];河南理工大学;2016年

2 孙佳楠;不同煤样变压解吸规律实验研究[D];河南理工大学;2016年

3 祁晨君;冷冻取芯过程煤芯变温规律模拟测试研究[D];河南理工大学;2016年

4 周一峰;温压作用下煤体破坏裂隙演化规律的研究[D];西安科技大学;2017年

5 任喜超;酸浸颗粒煤瓦斯解吸扩散规律实验研究[D];河南理工大学;2016年

6 丁智超;水分对阜康矿区低阶煤瓦斯放散特性影响的实验研究[D];西安科技大学;2017年

7 付启超;含瓦斯煤蠕变渗流规律与微观结构响应[D];河南理工大学;2016年

8 周市伟;构造煤瓦斯解吸扩散与吸附扩散实验研究[D];河南理工大学;2016年

9 张剑辉;煤中硫酸盐热化学还原反应成生H_2S气体的规律模拟研究[D];河南理工大学;2016年

10 张加琪;煤结构对软硬煤瓦斯放散规律差异性的影响[D];河南理工大学;2016年

，

本文编号：2031647