海泡石提纯改性及在内墙涂覆材料中的应用研究

发布时间：2018-08-27 10:00

【摘要】：针对湘潭海泡石原矿进行了提纯和改性处理,去除海泡石内部的石英、方解石等脉石矿物,以疏通其孔道结构,比表面积提升至156.9 m2/g,大幅增强吸附性能。利用改性海泡石制备内墙涂覆材料将显著提高涂料涂层对室内装修建材释放的甲醛等有害气体分子的吸附和固化效果和对室内空气环境湿度的调节性能,充分发挥海泡石涂料产品的功能性。研究了海泡石提纯改性工艺及其在内墙涂覆材料中的应用,验证了涂料样品对甲醛的吸附性,拓展了海泡石高附加值材料化应用的范畴。
[Abstract]:The sepiolite ore in Xiangtan was purified and modified to remove the gangue minerals such as quartz calcite and so on in order to dredge its pore structure and its specific surface area was raised to 156.9 m2 / g. The adsorption property was greatly enhanced. The preparation of inner wall coating material by modified sepiolite will significantly improve the adsorption and curing effect of coating on formaldehyde and other harmful gas molecules released from indoor decoration building materials, as well as the adjusting performance of indoor air humidity. Give full play to the functionality of sepiolite paint products. The purification and modification process of sepiolite and its application in the coating material of inner wall were studied. The adsorption of formaldehyde on the coating sample was verified and the application scope of high added value material of sepiolite was expanded.
【作者单位】： 湘潭源远海泡石新材料股份有限公司;湘潭海泡石科技有限公司;湘潭市海泡石功能材料工程技术研究中心;
【分类号】：TD97;TQ637

【相似文献】

相关期刊论文 前10条

1 花都;负离子内墙漆[J];建材工业信息;2004年08期

2 ;防氡内墙漆[J];化学建材;2001年03期

3 ;内墙干粉涂料[J];技术与市场;2002年07期

4 谢彩凤;;环保抗菌消醛内墙漆[J];现代营销(创富信息版);2005年04期

5 赵桂芝,肖德涛;内墙漆防氡效率测定方法的研究[J];核电子学与探测技术;2001年03期

6 ;石膏内墙粉刷材料[J];中国高校技术市场;1996年05期

7 冀志江,王静,田红,张连松;内墙建筑涂料的功能化[J];中国建材科技;2005年04期

8 李小戈，沈戮　;内墙钢化瓷性涂料的制备[J];湛江师范学院学报(自然科学版);1995年01期

9 ;托玛琳研发快速去除室内甲醛的内墙功能涂料[J];辽宁建材;2009年02期

10 王洪飞;可消除天花板及内墙表面裂纹的涂料[J];建材工业信息;2003年07期

相关重要报纸文章 前6条

1 王武;环保型负离子内墙漆问世[N];中国乡镇企业报;2004年

2 记者 单憬岗;我省率先研发出内墙节能保暖涂料[N];海南日报;2013年

3 本报记者 胡泉;首个内墙保暖涂料获住建部推广认证[N];中国房地产报;2013年

4 孙建华;孰优孰劣比比就知道[N];中国质量报;2003年

5 赵世喜;山东荣成推出建神牌内墙负离子健康漆[N];中国建材报;2004年

6 ;部分合格合成树脂乳液内墙涂料产品性状比较[N];中国质量报;2002年

相关硕士学位论文 前1条

1 胡晓光;海藻泥基功能型内墙乳胶漆的研制及其性能[D];华南理工大学;2015年

，

本文编号：2206945