草酸侵蚀红黏土水泥土复合体的试验研究

发布时间：2018-02-01 18:28

  本文关键词： 侵蚀机理 水泥土 草酸 浸泡试验　出处：《腐蚀科学与防护技术》2014年06期 　论文类型：期刊论文

【摘要】：采用p H值为2.5,3.5和4.0的草酸溶液,对红黏土水泥土复合体试样进行了长期浸泡(200 d),通过观测浸泡过程中,试样外观和耗酸量随时间的变化,分析了草酸对红黏土水泥土复合体的腐蚀和作用机理。结果表明:草酸对红黏土水泥土复合体的侵蚀为一个分解和重结晶过程,复合体中水泥水化产物和Fe2O3被分解,重结晶生成难溶的草酸钙(Ca C2O4)和草酸亚铁(Fe C2O4),最终使红黏土水泥土复合体中的骨架连接物由水泥水化产物转换为草酸钙和草酸亚铁。
[Abstract]:Using oxalic acid solution with pH value of 2.5% 3.5 and 4.0, the samples of red clay cement-soil complex were soaking for a long time for 200 days, and the soaking process was observed. The changes of appearance and acid consumption with time. The corrosion and mechanism of oxalic acid on red clay cement-soil complex are analyzed. The results show that the erosion of oxalic acid to red clay cement soil complex is a process of decomposition and recrystallization. The hydration products of cement and Fe2O3 were decomposed and recrystallized to form insoluble calcium oxalate Ca C 2O 4 and Fe Fe C 2O 4). Finally, the skeleton connectors in the red clay cement soil complex were converted from cement hydration products to calcium oxalate and ferrous oxalate.
【作者单位】： 昆明理工大学土木工程学院;
【基金】：国家自然科学基金项目(51108217)资助
【分类号】：TU41;TU52
【正文快照】： 1前言有机酸作为有机物残体分解、微生物代谢、植物根系分泌作用的产物之一,广泛分布于土体和地下水中。从均质土样测定的有机酸浓度并不一定很高但多变,且由于土层中有机物分布的不均性,较高浓度的有机酸微区总是存在的;有机酸作为众多工业生产中的原料或产品,其生产和使用过

【参考文献】

相关期刊论文 前9条

1 黄汉盛,鄢泰宁,兰凯;软土深层搅拌桩的水泥土抗腐蚀性室内试验[J];地质科技情报;2005年S1期

2 阮复昌,范娟,黄国水;各种草酸生产工艺的对比及我国草酸工业的现状[J];广东化工;1997年05期

3 宋志刚;张雪松;;稀硫酸侵蚀砂浆的试验研究[J];建筑材料学报;2012年02期

4 宁宝宽;金生吉;陈四利;;侵蚀性离子对水泥土力学特性的影响[J];沈阳工业大学学报;2006年02期

5 宁宝宽,陈四利,刘斌;水泥土的环境侵蚀效应与破裂过程分析[J];岩石力学与工程学报;2005年10期

6 白晓红;赵永强;韩鹏举;乔俊义;吴植安;;污染环境对水泥土力学特性影响的试验研究[J];岩土工程学报;2007年08期

7 韩鹏举;白晓红;赵永强;董晓强;任杰;;Mg~(2+)和SO_4~(2-)相互影响对水泥土强度影响的试验研究[J];岩土工程学报;2009年01期

8 杨俊杰;孙涛;张sュ，

本文编号：1482555