影响管线钢管抗氢致开裂性能的因素

发布时间：2018-04-13 00:06

  本文选题：管线钢管 + 氢致开裂　； 参考：《上海金属》2017年06期

【摘要】：采用NACE TM 0284—2003氢致开裂标准中的试验方法以及金相显微镜和扫描电镜,研究了显微组织、合金元素、硫含量、非金属夹杂物、轧制延伸率对管线钢管抗氢致开裂性能的影响。结果表明,非金属夹杂物是导致钢管氢致开裂的主要因素;具有铁素体+回火贝氏体组织的管线钢管抗氢致开裂性能优于具有铁素体+珠光体组织的钢管;增大轧制延伸率有利于提高钢管的抗氢致开裂性能;管线钢中的Ca/S比值为1.5~2.0时,钢管的抗氢致开裂性能较好;管线钢中添加铜和镍对调质态钢管的抗氢致开裂性能影响较小。
[Abstract]:Test method for cracking by using NACE standard TM 0284 - 2003 hydrogen and metallurgical microscope and scanning electron microscope, the microstructure of alloy elements, sulfur content, non-metallic inclusions, rolling elongation effect on pipeline steel resistance to hydrogen induced cracking performance. The results show that the non-metallic inclusions are the main factors leading to cracking of steel pipe hydrogen; steel pipeline steel with ferrite and tempered bainite HIC has better performance than ferrite + pearlite; increasing the rolling elongation rate is conducive to improve the pipe resistance to hydrogen induced cracking performance; the ratio of Ca/S pipeline steel in 1.5~2.0 steel, the performance of resistance to hydrogen induced cracking good; cracking effect of anti hydrogen addition of copper and nickel in pipeline steel on the quality state of steel tubes.

【作者单位】： 达力普石油专用管有限公司;河北省石油专用管工程技术研究中心;
【基金】：河北省科技计划项目(16211007D)
【分类号】：TE983

【相似文献】

相关期刊论文 前10条

1 饶庆华;谯永平;李和;陈中均;;低压放空分离器氢致开裂的探讨[J];电焊机;2011年01期

2 张旺峰,梁永芳,朱金华;石油专用管材的氢致开裂研究[J];西安公路交通大学学报;1998年03期

3 王玮,王春生,王忠,王纪兵;液化气球罐氢致开裂及修复[J];石油化工设备;1999年05期

4 张俊超;;氢致开裂试验及分析[J];中国高新技术企业;2009年12期

5 吴伟;韩进山;李效华;;集输管材应力导向氢致开裂实验评价[J];油气田地面工程;2012年10期

6 张琦;;腐蚀基本知识(三)[J];石油化工腐蚀与防护;1991年03期

7 张涛,李著信,苏毅,孙新岭;高强度管道钢氢致开裂门槛应力测定[J];油气储运;2002年08期

8 徐学利,辛希贤,仵亚婷,王建民;管线钢氢致开裂与冲击韧性的相关性[J];石油工程建设;2002年01期

9 尹成先,兰新哲,刘伟,霍春勇,冯耀荣;高强度天然气输送管抗氢致开裂试验研究[J];石油机械;2003年S1期

10 蔡黎波,蒋学良;油气分离器的硫化氢氢致开裂及防治措施[J];安徽化工;2003年06期

相关重要报纸文章 前2条

1 宏伟;油井管、管线管制造技术及产品特性[N];世界金属导报;2014年

2 王晓香;西气东输二线X80管线钢管及感应加热弯管国产化[N];世界金属导报;2009年

相关硕士学位论文 前1条

1 屈德强;基于应变设计高钢级管线钢管应变性能研究[D];西安石油大学;2011年

，

本文编号：1742031