磁性壳聚糖的制备及在三次采油中的应用

发布时间：2018-05-20 12:56

  本文选题：磁性颗粒 + 壳聚糖　； 参考：《现代化工》2017年11期

【摘要】：在分散有CoNiFe_2O_4磁性颗粒的壳聚糖溶液中,加入适量的戊二醛交联剂,制得内核为磁性CoNiFe_2O_4颗粒、外层包有壳聚糖的微米级磁性壳聚糖复合微球。用扫描电子显微镜、透射电子显微镜、红外光谱图、X射线衍射等方法对磁性壳聚糖微球的形态和组成特性进行分析。以CoNiFe_2O_4磁性壳聚糖作为驱油剂在油田进行驱油实验,结果表明,该驱油剂具有良好的驱油性能以及抗盐能力。
[Abstract]:In chitosan solution with dispersed CoNiFe_2O_4 magnetic particles, the magnetic CoNiFe_2O_4 particles were prepared by adding proper amount of glutaraldehyde crosslinking agent. The micrometer magnetic chitosan composite microspheres were coated with chitosan in the outer layer. The morphology and composition of magnetic chitosan microspheres were analyzed by means of scanning electron microscope, transmission electron microscope, infrared spectroscopy and X-ray diffraction. CoNiFe_2O_4 magnetic chitosan was used as oil displacement agent in oil field. The results showed that the flooding agent had good oil displacement performance and salt resistance.
【作者单位】： 中国石油管道局工程有限公司设计分公司;中国石油管道公司(管道销售公司);中国石油工程建设有限公司华北分公司;
【分类号】：O636.1;TE39

【相似文献】

相关期刊论文 前3条

1 陈宇;刘兆丽;吴庆辉;;微米级壳聚糖微球的制备[J];大连工业大学学报;2012年03期

2 党明岩;李俊杰;张晓磊;;改性壳聚糖微球的制备及其应用研究进展[J];沈阳理工大学学报;2014年02期

3 赵国骏,姜涌明,胡健,吉鑫松,钱雪明,袁中一;壳聚糖微囊的部分特性研究[J];功能高分子学报;1999年01期

相关博士学位论文 前2条

1 任春溶;磁性纳米复合材料的制备及其对重金属离子的吸附性能研究[D];浙江大学;2017年

2 张晓飞;几种核壳结构磁性材料的制备及其铀吸附性能[D];哈尔滨工程大学;2014年

相关硕士学位论文 前10条

1 高扬;载药壳聚糖类微球的制备及其释药性能研究[D];河北联合大学;2014年

2 李志华;壳聚糖印迹树脂的制备及吸附性能研究[D];沈阳理工大学;2015年

3 周赛春;壳聚糖键合硅胶的制备及其对Cr(Ⅵ)吸附的研究[D];浙江大学;2015年

4 孙晋伟;多孔壳聚糖微球培养hAMSCs及其负载Ⅰ型胶原多肽[D];湘潭大学;2012年

5 孟阳;疏水改性海藻酸钠的载药释药性能及其与壳聚糖的协同絮凝作用[D];青岛科技大学;2016年

6 罗肃霜;TiO_2/壳聚糖/氧化石墨烯复合微粒的制备及吸附砷研究[D];湖南大学;2015年

7 李济祥;壳聚糖基多孔微球的制备及其止血性能的研究[D];福建师范大学;2016年

8 万威;基于谷氨酸修饰磁性粒子对BSA的吸附研究[D];陕西师范大学;2016年

9 尹中华;京尼平交联制备5-Fu-壳聚糖微球及其体外释放研究[D];南昌大学;2014年

10 杨丽群;新型交联壳聚糖微球的制备及其在食品重金属检测中的应用[D];浙江工商大学;2011年

，

本文编号：1914706