炼厂静设备的腐蚀与防护

发布时间：2018-06-05 19:48

  本文选题：静设备 + 腐蚀　； 参考：《大连理工大学》2015年硕士论文

【摘要】：本篇论文经过对炼油厂通常所使用的金属静装备,比如换热器,工艺管线的腐蚀以及原油储罐等其它问题进行研究,发现腐蚀的表面现象,寻找出腐蚀真正的原因,并且给出相应的解决建议,避免或减少腐蚀情况的出现。第一,对于换热器管束的腐蚀问题,建议运用防腐7910涂料方法,解决了腐蚀问题。第二,对于储罐类设备主要分析了原油储罐的腐蚀发生的机理,提出采用厚浆型环氧玻璃鳞片抗静电涂料方法,解决腐蚀问题。第三,对地上工艺管线与埋地管线的腐蚀情况进行分析,探究了带保温的工艺管线的腐蚀状况,寻找出腐蚀的原因以及相应的解决办法；对埋地管线采用环氧煤沥青外加电流阴极保护结合的方式解决了腐蚀问题。
[Abstract]:Through the study of the metal static equipment commonly used in refineries, such as heat exchanger, corrosion of process pipeline and crude oil storage tank, the surface phenomenon of corrosion is found and the real reason of corrosion is found out in this paper. And gives the corresponding solution suggestion, avoids or reduces the corrosion situation appearance. Firstly, the corrosion problem of heat exchanger tube bundles is solved by using anticorrosive 7910 coating method. Secondly, the corrosion mechanism of crude oil storage tank is analyzed, and the method of thick slurry epoxy glass flake antistatic coating is put forward to solve the corrosion problem. Thirdly, the corrosion situation of the above ground process pipeline and buried pipeline is analyzed, and the corrosion condition of the process pipeline with heat preservation is explored, the reason of corrosion and the corresponding solution are found out. The corrosion problem of buried pipeline is solved by using epoxy coal pitch combined with current cathodic protection.
【学位授予单位】：大连理工大学
【学位级别】：硕士
【学位授予年份】：2015
【分类号】：TE986

【相似文献】

相关期刊论文 前5条

1 赵鑫辉;王娟娟;;烃处理静设备常见故障处理[J];中国石油和化工标准与质量;2013年17期

2 张东玲;焦虹;;浅谈化工静设备安装施工技术[J];黑龙江科技信息;2014年11期

3 王刚强;陈江;;石油化工企业静设备完整性管理技术研究[J];现代化工;2014年06期

4 李毅;詹燕民;轩军厂;吴奇兵;;基于RBI技术的海上平台延期服役静设备定量化安全评估技术[J];中国安全生产科学技术;2013年10期

5 ;[J];;年期

相关硕士学位论文 前1条

1 王磊;炼厂静设备的腐蚀与防护[D];大连理工大学;2015年

，

本文编号：1983210