Φ815mm法兰盘断裂失效分析

发布时间：2018-09-09 09:57

【摘要】：法兰盘是石油井口设备中的关键零件。根据准815mm法兰盘的工况,采用力学性能检测、显微组织和断口分析等方法对其断裂失效的原因进行了分析。结果表明:由于法兰盘组织中存在混晶,降低其力学性能;同时,由于热加工工艺不当,使热应力在厚大部位依次累积增大超过其热强度而产生微裂纹,在加压试验时,应力诱发引起裂纹快速扩展,沿径向从中间向两边扩展而断裂失效。
[Abstract]:The flange is the key part in the oil well head equipment. According to the working conditions of the quasi 815mm flange, the causes of fracture failure were analyzed by means of mechanical property test, microstructure analysis and fracture analysis. The results show that due to the existence of mixed crystals in flange structure, the mechanical properties of flange flanges are reduced, and at the same time, due to improper hot working technology, the thermal stress accumulates and exceeds its thermal strength in order to produce microcracks in the thick and large parts of the flange. Stress induced crack propagates rapidly and propagates from middle to both sides along radial direction, which leads to fracture failure.
【作者单位】： 重庆文理学院新材料技术研究院;重庆理工大学材料科学与工程学院;重庆新泰机械有限责任公司;
【分类号】：TG111.91

【相似文献】

相关会议论文 前10条

1 谭震;宫苹;赵青;;种植体断裂失效分析[A];第四届全国口腔种植学术会议论文集[C];2005年

2 郭瑞萍;赵兴国;张绍远;;道岔锁闭铁断裂失效分析[A];第十二届全国电子显微学会议论文集[C];2002年

3 朱锦艳;;内燃机阀门断裂失效分析[A];第三届全国扫描电子显微学会议论文集[C];2003年

4 段明南;周永;张永杰;;沉没辊轴头的过早断裂失效分析[A];2007中国钢铁年会论文集[C];2007年

5 朱锦艳;范文秉;陈丽芳;;深井管道断裂失效分析[A];第十二届全国电子显微学会议论文集[C];2002年

6 吴海平;;圆头螺钉断裂失效分析[A];2006'全国兄弟省市理化检测与质量控制学术交流会论文集[C];2006年

7 陈康敏;徐红兵;潘励;许晓静;;酒槽干燥机不锈钢列管断裂失效分析[A];第三届全国扫描电子显微学会议论文集[C];2003年

8 刘德林;张卫方;李春光;缪宏博;;某发动机高压二级涡轮叶片断裂失效分析[A];2007年全国失效分析学术会议论文集[C];2007年

9 李春光;姜涛;张卫方;;某连杆断裂失效分析[A];2007年全国失效分析学术会议论文集[C];2007年

10 万佳;蔡亚萍;;活塞杆断裂失效分析[A];2007四川省理化检验、无损检测学术交流年会论文集[C];2007年

相关硕士学位论文 前1条

1 张林;渣油泵叶轮数值模拟及断裂失效分析[D];华东理工大学;2013年

，

本文编号：2232052