数值模拟油气管线弯管处固液两相流场特性及冲刷腐蚀预测

发布时间：2018-11-22 13:37

【摘要】：为了定量描述输油管线弯管处由于流体方向改变引起的流场特性变化和管道内部冲蚀损伤过程,在Workbench平台下利用Fluent建立了90°弯管冲蚀物理模型,获得了弯管管壁压力、剪切应力以及流体流速的分布规律。结果表明:弯管处流场变化复杂,是此处管道严重冲刷腐蚀的原因;弯管外侧冲刷腐蚀最为严重,出口直管段的冲刷腐蚀次之,入口直管段及弯管内侧几乎无冲刷腐蚀;较大直径的砂粒会携带更大的动能和冲击力,从而在管壁上形成更加严重的冲刷腐蚀。
[Abstract]:In order to quantitatively describe the change of flow field characteristics and the process of internal erosion damage caused by the change of fluid direction at the bend of oil pipeline, a 90 掳pipe erosion physical model was established by using Fluent on Workbench platform, and the wall pressure of the bend pipe was obtained. The distribution of shear stress and fluid velocity. The results show that the complex flow field change in the bend is the cause of the serious erosion corrosion of the pipe, the external erosion corrosion is the most serious, the outlet straight pipe section is the second, the inlet straight pipe section and the inner side of the elbow have almost no scour corrosion. The larger diameter sand will carry more kinetic energy and impact force, resulting in more serious erosion corrosion on the pipe wall.
【作者单位】： 中国石油西南油气田公司川西北气矿;四川大学建筑与环境学院;
【分类号】：TE988.2

【相似文献】

相关期刊论文 前10条

1 Baotong Lu;;油气生产中的冲刷腐蚀(一)(英文)[J];石油与天然气化工;2013年01期

2 Baotong Lu;;油气生产中的冲刷腐蚀(二)(英文)[J];石油与天然气化工;2013年02期

3 吕露;欧阳传湘;张伟;;水力喷砂压裂过程喷嘴冲刷腐蚀数值计算[J];腐蚀与防护;2012年04期

4 江克;杨铁成;陈学东;张玮;高增梁;;高温高流速环烷酸冲刷腐蚀流场数值模拟研究[J];压力容器;2010年10期

5 黄学宾;陈宗林;赵文轸;;气举油管材料冲刷腐蚀的因素研究[J];石油化工腐蚀与防护;2007年06期

6 苏毅;刘佳鹏;李湛涛;吴卓;;流砂条件下P110钢冲刷腐蚀规律研究[J];石油化工腐蚀与防护;2014年01期

7 邓晓辉;邓卫东;廖伍彬;张炜强;陈圣乾;;X65海底管线在多相流中的冲刷腐蚀[J];石油化工腐蚀与防护;2011年01期

8 魏丹;叶东;王献f ;陈长风;白真权;李鹤林;;含CO_2多相流相态的非均匀性对输油管冲刷腐蚀的影响[J];科技导报;2009年16期

9 李亮;申龙涉;范开峰;孙蕾;王玉福;杨中;;弯管中多相流冲刷腐蚀数值模拟[J];辽宁石油化工大学学报;2014年03期

10 柴永新;刘小辉;;减顶冷却器的腐蚀与防护对策[J];广东化工;2014年16期

相关硕士学位论文 前2条

1 王凯;油井管材料液固两相流体冲刷腐蚀研究[D];西安石油大学;2013年

2 张昆;油气管道冲刷腐蚀与防护对策研究[D];东北石油大学;2013年

，

本文编号：2349528