基于丙烯酰胺系列新型水凝胶的合成与膨胀性能

发布时间：2018-08-24 15:34

【摘要】：通过自由基聚合方法合成聚丙烯酰胺(PAAM)水凝胶、丙烯酰胺(AAM)与甲基丙烯酸(MAA)的不同摩尔比的P(AAM-co-MAA)水凝胶,并对这些水凝胶的形貌和膨胀性能及pH敏感性能进行研究。结果表明,相比PAAM水凝胶,P(AAM-co-MAA)水凝胶的膨胀性能提高,但当AAM与MAA摩尔比为13∶2时,P(AAM-co-MAA)水凝胶具有更好的膨胀性和pH敏感性。这些水凝胶的特殊性能使它们有望应用于药物的缓控释放方面。
[Abstract]:Polyacrylamide (PAAM) hydrogels and P (AAM-co-MAA) hydrogels with different molar ratios of acrylamide (AAM) and (MAA) methacrylate were synthesized by free radical polymerization. The morphology, swelling properties and pH sensitivity of these hydrogels were studied. The results showed that the swelling property of P (AAM-co-MAA) hydrogel was higher than that of PAAM hydrogel, but when the molar ratio of AAM to MAA was 13:2, the swelling property and pH sensitivity of AAM (AAM-co-MAA) hydrogel were better. The special properties of these hydrogels make them promising for slow release of drugs.
【作者单位】： 渭南师范学院化学与生命科学学院;
【基金】：国家自然科学基金项目(51172136) 陕西省教育厅科学研究项目(11JK0579) 军民融合发展基金项目(13JMR20)
【分类号】：R318.08

【相似文献】

相关期刊论文 前7条

1 董宏伟;石四箴;陈克恭;小园凯夫;;快速加热型石膏包埋料对铸造精度影响的研究[J];口腔医学;2007年04期

2 巢永烈,邝先昊,廖运茂,王航;钛合金粉浆涂塑底层冠用耐火代型材料的膨胀性能测试[J];华西口腔医学杂志;1999年01期

3 陈鹏;林建华;李柱来;李贵双;叶晓;;聚甲基丙烯酸-2-羟乙酯水凝胶载药(类软骨)膜的制备及性能[J];中国组织工程研究与临床康复;2009年12期

4 范德增!100083,莫宣学!100081,翁润生!100081,秦飞!100081;磷酸盐包埋材料研究[J];北京口腔医学;2000年01期

5 李凌冰,谭业邦,孟建文;丙烯酰胺与葡萄糖烯丙基酰胺共聚水凝胶的合成与释药性能研究[J];生物医学工程学杂志;2004年06期

6 于炜婷;刘袖洞;李晓霞;綦文涛;任东文;马小军;;壳聚糖溶液pH对载细胞海藻酸钠-壳聚糖微胶囊性能的影响[J];高等学校化学学报;2006年01期

7 刘东阳;彭玉平;曾浩;;经蝶颅底重建材料的实验研究[J];中国医学物理学杂志;2011年02期

相关会议论文 前1条

1 李志宏;武继民;汪鹏飞;黄姝杰;关静;郭春;郭勇;李瑞欣;张西正;;高膨胀止血海绵的制备及性能研究[A];天津市生物医学工程学会第29届学术年会暨首届生物医学工程前沿科学研讨会论文集[C];2009年

相关博士学位论文 前2条

1 王伟强;冠状动脉支架力学行为有限元分析及其结构优化[D];大连理工大学;2006年

2 李宁;冠状动脉支架力学性能数值研究与优化设计[D];大连理工大学;2011年

相关硕士学位论文 前1条

1 斯清庆;明胶—几丁糖交联膜的制备及防粘连功能的实验研究[D];第二军医大学;2003年

，

本文编号：2201257