辅助性胶凝材料对混合水泥水化和耐久性的影响:化学与物理原理（英文）

发布时间：2018-03-07 18:55

  本文选题：辅助性胶凝材料　切入点：反应　出处：《硅酸盐学报》2015年10期 　论文类型：期刊论文

【摘要】：采用物理和化学方法考察了添加辅助性胶凝材料对水泥水化和耐久性的影响。根据辅助性胶凝材料的相似性和差异性将其分为潜在水化性、火山灰活性,并可进一步分为硅酸盐类、铝酸盐类、碳酸盐类等。还研究了包括辅助性胶凝材料与添加剂之间的相互作用,如减水剂、促凝剂等。结果表明:添加辅助性胶凝材料对混凝土耐久性有一定影响,如抗氯离子渗透、抗碳化、碱骨料反应,以及抗硫化物腐蚀等。在相同水胶比时,添加辅助性胶凝材料有助于提高混凝土的抗老化性能。但碳化作用除外,这可以通过降低水胶比来提高混凝土的耐久性。
[Abstract]:The effects of auxiliary cementitious materials on the hydration and durability of cement were investigated by physical and chemical methods. According to the similarity and difference of auxiliary cementitious materials, they were divided into latent hydration and pozzolanic activity. It can be further divided into silicate, aluminate, carbonate, etc. The interaction between additive and auxiliary cementitious material, such as water-reducing agent, is also studied. The results show that the addition of auxiliary cementitious materials has a certain effect on the durability of concrete, such as resistance to chloride ion penetration, carbonation resistance, alkali aggregate reaction, and corrosion resistance to sulphide, etc. At the same water / binder ratio, The addition of auxiliary cementitious materials can improve the aging resistance of concrete, except carbonation, which can improve the durability of concrete by reducing the water-binder ratio.
【作者单位】： SINTEF
【分类号】：TQ172.11

【共引文献】

相关期刊论文 前10条

1 刘超;马忠诚;刘浩云;;水泥混凝土硫酸盐侵蚀综述[J];材料导报;2013年07期

2 赵瑞;史才军;王小刚;吕奎喜;何稳;;碱激发胶凝材料与硅酸盐水泥基材料碱骨料反应的比较[J];硅酸盐通报;2013年09期

3 金勇刚;袁庆莲;王勇飞;;粉煤灰部分取代石灰石粉的水泥胶砂干缩性能研究[J];粉煤灰;2013年05期

4 周维;周卫兵;孙正;李小超;喻巍;;醇胺类外加剂对大掺量混合材复合水泥水化过程的影响研究[J];建材世界;2013年05期

5 李相国;何超;罗忠涛;马保国;田振;谭洪波;;铝酸三钙的含量对含石灰石粉水泥浆体碳硫硅酸钙形成的影响(英文)[J];硅酸盐学报;2013年11期

6 陈晨;贡伟亮;李琴;翟建平;;粉煤灰碱浸出体系反应过程分析:Ⅱ反应动力学[J];环境科学与技术;2013年12期

7 钱觉时;韦迎春;邓铃夕;沈燕;侯鹏坤;;硅酸盐水泥中硫酸盐类型与作用[J];硅酸盐学报;2014年02期

8 黄天勇;王栋民;刘泽;王U，

本文编号：1580532