  本文选题：改性沥青　切入点：元素分析　出处：《硅酸盐通报》2014年06期 　论文类型：期刊论文

【摘要】：应用常规试验、元素分析、红外光谱分析和凝胶色谱分析研究沥青老化后的微观结构与沥青老化后性能之间的关系,综合几种测试和表征方法可知:相比PAV老化,RTFOT老化对埃索基质沥青性能影响不是特别大;整体上SBS埃索抗老化能力优于基质沥青。将元素分析、红外光谱分析和凝胶色谱分析三者有机结合起来可以相互补充,有利于分析沥青老化后的微观结构。
[Abstract]:The relationship between the microstructure of asphalt after aging and its properties after aging was studied by routine test, elemental analysis, infrared spectroscopy and gel chromatography. According to several test and characterization methods, compared with PAV aging, the effect of RTFOT aging on the performance of Esso matrix asphalt is not particularly great, and the overall anti-aging ability of SBS Esso is better than that of base asphalt. The combination of infrared spectroscopy and gel chromatography can complement each other, which is helpful to analyze the microstructure of asphalt after aging.
【作者单位】： 华南理工大学土木与交通学院;广西金盟工程有限公司;
【基金】：国家自然科学基金重点项目(51038004) 广东省交通运输厅科技项目(2010-02-004) 广西石化资源加工及过程强化技术重点实验室开放基金(2013K010)
【分类号】：TU535

【相似文献】

相关期刊论文 前6条

1 钱国桢,丁根明,张新国;沥青老化的防治及其在隔震垫中的应用[J];浙江建筑;2002年S1期

2 钱国桢,宋新初,丁根明,许刚;沥青老化的防治及其在隔震垫中的应用[J];工程抗震;2001年04期

3 王举才;;做好沥青油毡防水屋面的技术措施[J];建筑技术;1993年07期

4 马立殟;庞凌;吴少鹏;;光氧老化对沥青物理和化学性能的影响[J];广东建材;2007年11期

5 原健安，张登良;温度对胜利沥青热老化的影响[J];西安公路交通大学学报;1995年01期

6 王衡,王海;沥青混合料的老化机理分析[J];山西建筑;2005年09期

相关硕士学位论文 前1条

1 李凯涛;镁锌基水滑石在耐紫外老化沥青中的应用及其清洁工艺制备研究[D];北京化工大学;2013年

，

本文编号：1585546