高延性纤维混凝土抗压强度试验研究

发布时间：2017-12-28 09:30

本文关键词：高延性纤维混凝土抗压强度试验研究　出处：《建筑结构》2016年23期 　论文类型：期刊论文

【摘要】：通过9组不同配合比高延性纤维混凝土立方体和棱柱体试块的抗压强度试验,研究不同尺寸高延性纤维混凝土立方体与棱柱体抗压强度之间的关系。结果表明,高延性纤维混凝土试块纵向受压时表现出良好的抗压韧性;高延性纤维混凝土强度比值系数随着材料延性的提高而增大,水胶比和粉煤灰掺量增大,强度比值系数有所提高;试验得到截面为100,70.7,40mm的高延性纤维混凝土试块强度比值系数分别为0.91,0.88,0.80。根据试验结果,提出了高延性纤维混凝土的轴心抗压强度计算公式。
[Abstract]:The compressive strength of 9 groups of high strength fiber concrete cube and prism specimen with different mixing ratios is studied, and the relationship between cube compressive strength and cube prism compressive strength of different sizes of high ductility fiber concrete is studied. The results show that the high ductility of fiber concrete specimens under axial compression showed good compressive toughness; high ductility fiber reinforced concrete strength ratio increases with increasing the ductility of the material, water binder ratio and fly ash content increased, the ratio of intensity coefficient increased; the test section for high ductility 100,70.7,40mm fiber concrete strength ratio the coefficient were 0.91,0.88,0.80. Based on the test results, the formula for calculating the axial compression strength of high ductility fiber concrete is proposed.
【作者单位】：西安建筑科技大学土木工程学院;成都天华西南建筑设计有限公司;
【基金】：陕西省自然科学基金项目(2013JM7013) 西安市科技计划项目(CX13135-3)
【分类号】：TU528.572
【正文快照】： 2成都天华西南建筑设计有限公司,成都610016)0前言高延性水泥基复合材料是一种具有高韧性、高抗裂性能和耐损伤能力的新型结构材料,在拉伸和剪切荷载作用下具有多裂缝开展和应变硬化特征,能显著改善混凝土的脆性,提高构件的抗震性能,具有广泛的应用前景。美国Li V C教授[1-3]

【相似文献】