超高抗折钢纤维混凝土配制及工程应用

发布时间：2018-01-25 14:15

本文关键词： 超高抗折泵送混凝土高性能复合掺合料　出处：《新型建筑材料》2017年09期 　论文类型：期刊论文

【摘要】：结合工程实例,采用特制钢纤维、高性能复合掺合料等原材料进行配合比设计,通过混凝土配合比正交试验,以混凝土施工性能和力学性能作为评价指标,优化了砂率、水胶比、胶凝材料用量、钢纤维掺量等影响因素。试验结果和工程应用表明,特制钢纤维能显著提高混凝土的抗折强度,高性能复合掺合料能改善拌合物的粘聚性,按照砂率为41%,水胶比为0.30,钢纤维体积掺量为2.5%,胶凝材料用量为630 kg/m~3的配合比,能够配制出抗折强度达到20 MPa的超高抗折钢纤维混凝土。
[Abstract]:Combined with engineering example , the mix proportion design of special steel fiber and high performance composite admixture was adopted . The influence factors such as sand ratio , water - cement ratio , amount of cementing material and amount of steel fiber were optimized by orthogonal test . The experimental results and engineering application show that the special steel fiber can obviously improve the flexural strength of concrete , the cement ratio is 0.30 , the volume of steel fiber is 2.5 % , the amount of cementing material is 630 kg / m ~ 3 , and it is possible to prepare the ultra - high bending - resistant steel fiber concrete with the flexural strength of 20 MPa .

【作者单位】：四川华西绿舍建材有限公司;
【分类号】：TU528.572
【正文快照】： 0 引言钢纤维混凝土是在普通混凝土中掺入乱向分布的钢纤维所形成的一种新型多相复合材料。这些乱向分布的钢纤维能够有效地抑制混凝土内部微裂缝的扩展及宏观裂缝的形成,显著地改善了混凝土的抗裂、抗冲击及抗疲劳性能[1-2],钢纤维混凝土具有较好的延性以及动力性能[3-4]。

【相似文献】