PVA-纤维素混杂纤维混凝土的工作性能与力学性能
本文选题：PVA纤维 切入点：纤维素纤维 出处：《混凝土》2017年10期 论文类型：期刊论文
【摘要】：设计了强度等级为C40的PVA-纤维素混杂纤维混凝土,通过试验研究分析了PVA-纤维素混杂纤维对混凝土拌合物坍落度、抗压强度、劈裂抗拉强度的影响。研究表明:PVA-纤维素混杂纤维混凝土拌合物坍落度主要受PVA纤维影响,PVA纤维掺量越高,混凝土坍落度损失越大;PVA、纤维素纤维的掺量和比例不同,混杂纤维的增强效果也不同,当PVA和纤维素纤维按1.2 kg/m~3+0.9 kg/m~3混杂时,混凝土的抗压强度和劈裂抗拉强度最高;PVA-纤维素混杂纤维混凝土的抗压强度与劈裂抗拉强度具有较好的幂函数相关关系。
[Abstract]:PVA- cellulose hybrid fiber concrete with strength grade C40 was designed, and the slump and compressive strength of concrete mixed with PVA- cellulose hybrid fiber were analyzed by experiment. The study shows that the slump of concrete mixed with PVA fiber is mainly affected by the content of PVA fiber, the greater the loss of slump of concrete is, the greater the content and proportion of cellulose fiber is. The reinforcing effect of hybrid fibers was also different, when PVA and cellulose fibers were mixed at 1.2 kg/m~3 0.9 kg/m~3, The compressive strength and splitting tensile strength of concrete are the highest. The compressive strength of PVA- cellulose hybrid fiber reinforced concrete has a good power function correlation with the splitting tensile strength.
【作者单位】： 宁波工程学院;郑州市工程质量监督站;郑州市市政工程管理处;
【基金】：国家自然科学基金项目(51408553) 河南省重点科技攻关计划项目(152102210033) 郑州大学优秀青年教师发展基金(1521322003)
【分类号】：TU528.572
【相似文献】
相关期刊论文 前10条
1 郭靓;;浅谈混杂纤维混凝土的增强机理[J];科技信息;2011年03期
2 张冲;宁博;;混杂纤维混凝土地铁管片数值模拟研究[J];混凝土与水泥制品;2012年10期
3 方和江;李新;;混杂纤维混凝土疲劳试验研究[J];建材世界;2010年06期
4 王量;鞠丽艳;胡春花;;混杂纤维高性能混凝土配合比优化设计[J];城市道桥与防洪;2006年04期
5 宁博;欧阳东;易宁;鲁刘磊;易承波;潘攀;吴亭亭;;混杂纤维混凝土在地铁管片中的应用[J];混凝土与水泥制品;2011年01期
6 王海超;刘校源;;较高韧性混杂纤维混凝土弯曲抗拉性能试验研究[J];混凝土与水泥制品;2011年04期
7 李永鹏;嵇绍华;何锐;陈拴发;;细集料对混杂纤维混凝土性能的影响[J];混凝土;2013年06期
8 夏冬桃;周博儒;刘向坤;杨应平;;低掺量三元混杂纤维混凝土轴拉性能试验[J];华中科技大学学报(自然科学版);2013年11期
9 李习波;焦楚杰;高俊岳;王龙;艾武波;;混杂纤维混凝土研究进展[J];低温建筑技术;2014年01期
10 陈家来;;混杂纤维混凝土抗弯冲击性能[J];科技促进发展;2010年S1期
相关会议论文 前3条
1 朋改非;康义荣;;高温对混杂纤维活性粉末混凝土力学性能的影响[A];2013年混凝土与水泥制品学术讨论会论文集[C];2013年
2 燕兰;邢永明;郝，
本文编号：1578855
本文链接：https://www.wllwen.com/jianzhugongchenglunwen/1578855.html