氧化石墨烯对水泥水化产物及聚集状态的调控作用

发布时间：2018-04-03 04:16

  本文选题：氧化石墨烯　切入点：水泥水化产物　出处：《精细化工》2017年05期

【摘要】：通过对石墨的氧化及超声波分散制备了氧化石墨烯(GO)纳米片层,采用FTIR、XPS、SEM、AFM对其结构进行了表征。测试结果表明:GO纳米片层尺寸为100~800 nm,GO上羟基和羧基的质量分数分别为22.1%和29.4%。将GO掺入水泥基复合材料,在GO的加入质量为水泥质量的0.03%时,水泥基体主要由多面体状晶体通过交织、嵌入等方式聚集而成,形成了具有花型形貌的微观结构,与空白样比较,其28 d时平均抗折强度和抗压强度分别增加了93.9%和80.0%。
[Abstract]:Graphene oxide nanocrystalline oxide (GOO) was prepared by oxidation of graphite and ultrasonic dispersion, and its structure was characterized by FTIRN XPSN SEMMA-AFM.The results show that the mass fraction of hydroxyl group and carboxyl group on the layer is 22.1wt% and 29.4wt% respectively.When go was added into cement matrix composites, when the mass of go was 0.03% of cement mass, the cement matrix was mainly composed of polyhedron crystals by interleaving and embedding, thus forming the microstructure with floral morphology.Compared with the blank sample, the average flexural strength and compressive strength increased by 93.9% and 80.0% at 28 days, respectively.
【作者单位】： 陕西科技大学轻工科学与工程学院;陕西科技大学化学与化工学院;南通新型建筑材料有限公司;
【基金】：国家自然科学基金面上项目(21276152) 陕西省科技统筹资源引导项目(2016KTCL01-14)~~
【分类号】：TU528.572

【参考文献】

中国期刊全文数据库 前8条

1 张伟;宗兰;张士萍;;纤维混杂技术对高性能混凝土的早期抗裂性的影响[J];混凝土;2016年08期

2 赵海锋;吕生华;邓丽娟;;氧化石墨烯增强增韧水泥基复合材料的结构和性能[J];陕西科技大学学报(自然科学版);2016年03期

3 吕生华;李莹;赵浩然;贺亚亚;邓丽娟;朱琳琳;贾春茂;;氧化石墨烯在水泥基体中的分散性及对其结构和性能的影响[J];精细化工;2016年05期

4 刘琼;许清风;李向民;;石墨烯和碳纳米管水泥基复合材料研究进展[J];混凝土与水泥制品;2016年03期

5 王德辉;史才军;吴林妹;;超高性能混凝土在中国的研究和应用[J];硅酸盐通报;2016年01期

6 王辉;刘爱红;李航;;石墨烯纳米片对水泥基复合材料力学性能的影响[J];混凝土与水泥制品;2015年12期

7 李庆华;周宝民;黄博滔;徐世p，

本文编号：1703579