新型链烷醇胺对水泥水化硬化的影响

发布时间：2018-04-11 23:00

  本文选题：链烷醇胺 + 水泥　； 参考：《硅酸盐学报》2017年08期

【摘要】：以二乙醇单异丙醇胺DEIPA、—乙醇二异丙醇胺EDIPA、N,N,N',N'-四(2-羟基乙基)-乙二胺THEED和N,N,N',N'-四(2-羟丙基)-乙二胺THEED为化学添加剂,研究了其对水泥水化过程、含气量及硬化浆体性能的影响及机理。结果表明:DEIPA、EDIPA能显著提高水泥砂浆各龄期强度,分别在3 d和56 d提高4.4%和10.4%,并促进水泥水化进程,同时其对AFt向AFm转化的加速作用能有效降低孔隙率,优化孔径分布;THEED、THPED可促进水泥水化,其引气性对砂浆早期强度增进不利,但有利于后期强度提高,同时掺量范围比DEIPA和EDIPA更宽。
[Abstract]:Effect and mechanism of gas content and properties of hardened slurry.The results showed that the strength of cement mortar increased by 4.4% and 10.4% at 3 d and 56 d, respectively, and promoted the hydration process of cement. At the same time, the accelerated conversion of AFt to AFm could effectively reduce the porosity of cement mortar.Optimization of pore size distribution can promote hydration of cement, and its air entrainability is disadvantageous to the increase of early strength of mortar, but it is propitious to increase the later strength of mortar, and the range of mixing amount is wider than that of DEIPA and EDIPA.
【作者单位】： 南京工业大学材料科学与工程学院;材料化学工程国家重点实验室;
【基金】：国家自然科学青年基金(No.51202109) 国家863计划项目(No.2015AA034701) 江苏高校优势学科建设工程项目
【分类号】：TQ172.1

【相似文献】

相关期刊论文 前10条

1 翟彦青;徐新;蒋力培;;醇胺溶液吸收二氧化碳的实验研究[J];化学通报;2009年07期

2 陆诗建;李清方;张建;;醇胺溶液吸收二氧化碳方法及反应原理概述[J];科技创新导报;2009年13期

3 韩江则;刘有智;祁贵生;;有机醇胺溶液脱除硫化氢气体的研究进展[J];化工中间体;2010年05期

4 山东胜利石化总厂科研所情报室化工组;;苯菲尔法脱除酸性气发展近况[J];胜利石油化工;1979年01期

5 景晓燕,董吉川,张密林,刘顺隆;醇胺吸收和解吸CO_2的研究[J];化学工程师;1999年05期

6 卢敏;武斌;朱家文;杨安;;醇胺有机溶液吸收和解吸CO_2的研究[J];石油与天然气化工;2006年02期

7 庞晓华;陶氏化学计划新建特种链烷醇胺生产装置[J];精细石油化工进展;2005年04期

8 李伟峰;马素花;沈晓冬;;链烷醇胺对水泥长期储存性能及粉体性能的影响[J];水泥;2014年07期

9 陆建刚;郑有飞;陈敏东;王连军;;有机醇胺溶液吸收选择性脱除H_2S[J];天然气化工(C1化学与化工);2007年06期

10 马俊;李进龙;彭昌军;刘洪来;胡英;;基于黏滞球模型的CPA状态方程应用于醇胺系统相平衡的计算[J];化工学报;2010年07期

相关硕士学位论文 前3条

1 何清;状态方程模拟醇胺系统的热力学性质[D];华东理工大学;2010年

2 华雪莹;醇胺水溶液粘度的实验和理论研究[D];华北电力大学;2012年

3 史澄辉;醇胺溶液CO_2吸收性能与解吸能耗实验研究[D];青岛科技大学;2013年

，

本文编号：1738022