建筑多孔材料太阳能蒸发冷却性能动态实验研究

发布时间：2018-07-02 19:45

  本文选题：多孔材料 + 太阳辐射　； 参考：《太阳能学报》2017年04期

【摘要】：采用风洞研究一种由多孔饰面层,防水砂浆层和混凝土基层组成的复合试件在动态工况下的蒸发冷却性能。研究结果表明:风洞实验段各环境参数测量值与环境控制系统设定值之间的归一化均方根误差小于4%;湿试件饰面层的蒸发过程在白天时间段可累计消耗约80%的短波辐射热量;干、湿试件饰面层的反照率分别为0.406±0.040和0.181±0.018。
[Abstract]:The evaporative cooling performance of a composite specimen composed of a porous finish layer, a waterproof mortar layer and a concrete base is studied in a wind tunnel under dynamic conditions. The results show that the normalized root mean square error between the measured values of the environmental parameters and the set values of the environmental control system is less than 4, and the evaporation process of the surface layer of the wet specimen can consume about 80% of the short-wave radiation heat during the daytime. The albedo of dry and wet specimens was 0.406 卤0.040 and 0.181 卤0.018 respectively.
【作者单位】： 华南理工大学化学与化工学院;华南理工大学建筑学院;华南理工大学电力学院;
【基金】：国家自然科学基金(51308223;51678243) 广东省自然科学基金(2016A030313506) 亚热带建筑科学国家重点实验室自主课题(2015ZC14)
【分类号】：TU50

【相似文献】

相关期刊论文 前10条

1 魏剑;桑国臣;;金属多孔材料在建筑领域的应用展望[J];热加工工艺;2009年22期

2 唐路平;;多孔材料的孔结构测试技术[J];重庆建筑工程学院学报;1983年03期

3 张巨松;;多孔材料强度模型的探讨[J];沈阳建筑工程学院学报;1988年03期

4 唐路平;;水泥混凝土多孔材料的强度与孔径分布的关系探讨[J];混凝土与水泥制品;1986年04期

5 唐路平;;多孔材料强度与孔径分布的定量关系[J];重庆建筑工程学院学报;1986年04期

6 陶高梁;张季如;黄丽;袁伦;;多孔材料孔隙特性的分形描述[J];建筑材料学报;2010年05期

7 刘伯伦,钟祥璋;提高多孔材料低频吸声性能的探讨[J];声学技术;1992年Z1期

8 卢军,陈启高;含盐多孔材料传热传质研究[J];重庆建筑大学学报;1999年06期

9 刘晓燕;郑春媛;黄彩凤;;多孔材料导热系数影响因素分析[J];低温建筑技术;2009年09期

10 余跃滨;张国强;余代红;严伟锋;;多孔材料污染物散发外部影响因素作用分析[J];暖通空调;2006年01期

相关会议论文 前2条

1 张玉;孟庆林;;多孔材料气候蒸发实验模型研究[A];建筑环境与建筑节能研究进展——2007全国建筑环境与建筑节能学术会议论文集[C];2007年

2 王金忠;王金海;;建筑多孔材料热质扩散系数的参数估计和测定方法的优化分析[A];土木工程计算机应用文集——中国土木工程学会计算机应用学会第五届年会论文集[C];1993年

相关硕士学位论文 前5条

1 米海惠;建筑外墙保温用空心微珠多孔材料的制备及性能研究[D];河北工程大学;2017年

2 何化岳;湿多孔材料被动防热技术研究[D];西安建筑科技大学;2006年

3 许伊那;多孔材料饰面建筑构件的被动蒸发冷却研究[D];华南理工大学;2012年

4 沈润霖;测量多孔材料含水、含冰量的热线法[D];大连理工大学;2014年

5 杨倩;基于分形理论的陶瓷隔（蓄）热多孔材料传热特性研究与应用[D];东华大学;2007年

，

本文编号：2090719