CdSZnO核壳纳米棒阵列结构的制备及在太阳能电池中的应用
发布时间:2018-01-06 00:01
本文关键词:CdSZnO核壳纳米棒阵列结构的制备及在太阳能电池中的应用 出处:《化工新型材料》2016年03期 论文类型:期刊论文
更多相关文章: ZnO纳米棒阵列 电沉积法 CdS纳米晶 太阳能电池
【摘要】:采用水热法制备垂直于FTO导电玻璃基底的ZnO纳米棒阵列,然后通过电化学沉积法在ZnO纳米棒阵列上沉积CdS纳米晶,形成CdS/ZnO核壳纳米棒阵列结构。利用扫描电子显微镜(SEM)、X射线衍射仪(XRD)、X射线能谱仪(EDS)和紫外-可见分光光度计(UV-Vis)等对所得样品的形貌、结构组成进行分析表征;并以其为光电极组装太阳能电池,研究CdS纳米晶厚度对该电池光电性能的影响。结果表明,所得样品不仅拓宽和加强电池的光吸收能力,也有效调控光生载流子的传输。当CdS纳米晶沉积时间为60s时,电池的光电转换效率最高可达1.10%。
[Abstract]:ZnO nanorods arrays perpendicular to FTO conductive glass substrates were prepared by hydrothermal method. Then CdS nanocrystals were deposited on ZnO nanorods by electrochemical deposition. The structure of CdS/ZnO core shell nanorod array was formed. The morphology and structure of the samples were characterized by X-ray energy spectrometer (EDS) and UV-Vis-UV spectrophotometer. The effect of the thickness of CdS nanocrystalline on the photovoltaic performance of the solar cell was studied. The results showed that the sample not only broadens and strengthens the photoabsorption ability of the cell. When the deposition time of CdS nanocrystalline is 60 s, the photovoltaic conversion efficiency can reach 1.10%.
【作者单位】: 辽宁工程技术大学理学院;矿山热动力灾害与防治教育部重点实验室辽宁工程技术大学安全科学与工程学院;
【基金】:国家科技支撑计划(2013BAK06B07) 辽宁省教育厅科学研究项目(L2013138)
【分类号】:TB383.1;TM914.4
【正文快照】: 量子点敏化太阳能电池作为第三代太阳能电池,具有生产成本低廉、工艺简单及稳定性好等优点,是近年来的研究热点之一。ZnO作为一种优异的无机半导体材料,成为太阳能电池研究较多的材料,但其禁带宽度约为3.2eV,仅吸收紫外光,这限制其对可见光的利用[1]。为进一步提高ZnO的光电性,