采用比表面积和孔径分析仪测量纳米颗粒粒径

发布时间：2018-03-02 00:11

  本文关键词： 纳米颗粒 粒径测量 比表面积 孔径分析仪　出处：《中国粉体技术》2017年04期 　论文类型：期刊论文

【摘要】：采用比表面积和孔径分析仪,利用颗粒堆积产生的孔隙大小与颗粒粒径之间存在的几何关系,通过测量纳米颗粒堆积产生的孔隙尺寸,实现了纳米颗粒粒径的测量。结果表明,对于粒径在30~70 nm的纳米颗粒,颗粒堆积产生的介孔尺寸与颗粒粒径之间存在良好的线性关系,通过工作曲线可快速获得粒径数值。尤其对于粒径小于100 nm的干燥颗粒,该方法具有良好的适用性,测量分辨率可达0.2 nm,测量结果具有统计意义。
[Abstract]:By using the specific surface area and pore size analyzer and the geometrical relationship between the pore size and the particle size, the particle size is measured by measuring the pore size generated by the particle accumulation. The results show that, There is a good linear relationship between the mesoporous size and the particle size when the particle size is 30 ~ 70 nm, and the particle size value can be obtained quickly by the working curve, especially for the dry particle with the diameter less than 100 nm. This method has good applicability, and the resolution of measurement is up to 0.2 nm. The results are of statistical significance.
【作者单位】： 中国科学院大连化学物理研究所催化基础国家重点实验室;
【基金】：国家自然科学青年科学基金项目,编号:21203190
【分类号】：TB302.1

【相似文献】

相关期刊论文 前1条

1 曹标,陈明,周崎;三种纳米颗粒粒径测量方法的比较[J];物理测试;2005年06期

相关会议论文 前2条

1 董亮;苏璇;;颗粒粒径、粒形分析的新方法——数字图像分析[A];第七届全国颗粒测试学术会议、2008上海市颗粒学会年会论文集[C];2008年

2 胡彦杰;宁靖卫;李春忠;丁宏秋;;多重射流燃烧反应器内轴向温度分布的数值模拟及其对纳米颗粒粒径的影响[A];颗粒学最新进展研讨会——暨第十届全国颗粒制备与处理研讨会论文集[C];2011年

相关博士学位论文 前1条

1 杨晖;基于后向动态光散射的高浓度纳米颗粒粒径测量技术的研究[D];上海理工大学;2009年

相关硕士学位论文 前1条

1 史跃岗;二氧化钛纳米颗粒粒径影响因素的研究[D];大连理工大学;2009年

，

本文编号：1554179