基于煤矸石构筑环境友好型阻燃EVA的性能研究

发布时间：2018-03-15 06:00

  本文选题：乙烯-乙酸乙烯共聚物　切入点：煤矸石　出处：《合成树脂及塑料》2017年01期 　论文类型：期刊论文

【摘要】：通过添加不同比例的煤矸石构筑环境友好型阻燃材料类水滑石(LDHs),X射线衍射结果显示LDHs结构完整。以乙烯-乙酸乙烯共聚物(EVA)为基体树脂,LDHs为复配阻燃剂制备EVA/LDHs复合材料。采用极限氧指数仪、锥形量热仪、烟密度测试仪等研究了复合材料的燃烧性能和抑烟性能,并探讨了相应的阻燃及抑烟作用机理。结果表明:EVA3[n(Mg2+)∶n(Al3+)为3∶1]的极限氧指数最高,达到28.30%;与纯EVA相比,EVA/LDHs复合材料的热释放速率、质量损失、烟生成速率均显著降低,表现出良好的阻燃性能;在点火和未点火情况下,复合材料均体现出良好的抑烟性能。
[Abstract]:By adding different proportion of coal gangue to build environment-friendly flame-retardant materials, the results of X-ray diffraction showed that the structure of LDHs was intact. The EVA/LDHs composite was prepared by using ethylene-vinyl acetate copolymer as matrix resin and flame retardant. Materials. Limit oxygen exponents, The combustion and smoke suppression properties of the composites were studied by cone calorimeter and smoke density tester. The flame retardancy and smoke suppression mechanism of the composites were also discussed. The results showed that the limit oxygen index of the composite was the highest when the ratio of% EVA3 was 3: 1. Compared with pure EVA, the heat release rate, mass loss and smoke formation rate of EVA / LDHs composites decreased significantly and showed good flame retardancy.
【作者单位】： 青岛科技大学环境与安全工程学院;
【基金】：国家自然科学基金资助项目(51572138);(51372129) 山东省自然科学基金(IR2013DQ002) 青岛市民生科技计划(14-2-3-70-nsc)
【分类号】：TQ325.12;TB332

【相似文献】

相关期刊论文 前10条

1 徐义清;;油田化工企业EVA的提升策略[J];油气田地面工程;2011年06期

2 ;“爱啦”,首创80后专属婚戒——访梦雅恒珠宝“爱啦”设计师EVA[J];中国黄金珠宝;2012年05期

3 潘群;;经济增加值(EVA)与会计诚信[J];武汉科技学院学报;2007年07期

4 李丽娜;吴春峰;高海梅;;油田企业实施EVA考核中存在的问题分析[J];能源技术与管理;2013年06期

5 王秀梅;;基于EVA的煤炭企业财务管理问题研究[J];煤炭经济研究;2011年06期

6 李志学;张昊;李萌;;国内三大油田企业EVA考核状况的对比分析[J];西南石油大学学报(社会科学版);2013年06期

7 葛文雷;企业经营业绩评价的EVA方法及调整计算[J];东华大学学报(自然科学版);2001年04期

8 吕苗苗;杨文杰;;基于EVA的煤炭上市企业经营业绩实证分析[J];上海商学院学报;2010年01期

9 梅海红;赵向琴;洪燕平;;基于EVA的企业绩效评价研究——以我国煤炭上市公司为例[J];黑龙江科技信息;2011年12期

10 姜远峰;;做足“减法”实现EVA最大化[J];中国石化;2011年07期

相关会议论文 前10条

1 张少平;陈U，

本文编号：1614706