高强高导Cu-Nb微观复合材料的尺寸效应

发布时间：2018-04-26 04:14

  本文选题：Cu-Nb + 高强度　； 参考：《稀有金属材料与工程》2017年03期

【摘要】：高强度高电导Cu-Nb微观复合材料具有纳米结构的Nb芯丝和纯Cu层,材料的尺寸效应促使力学性能呈规律变化。通过不同线材尺寸的应力应变曲线测试研究了材料强度随内部Nb芯丝尺寸的变化规律,通过纳米压痕手段分析了材料弹性模量和纳米压痕值随随材料尺寸的变化特征。结果表明,材料的强度实测值远大于混合定律计算的理论值,且随Nb芯丝尺寸的减小强度呈指数增加,Nb芯丝纳米硬度值也随尺寸的减小显著增加。与电子自由程相关的界面电子散射作用是影响材料电导的主要因素。
[Abstract]:High strength and high conductivity Cu-Nb microcomposites have nanostructured NB core wire and pure Cu layer. The size effect of the material makes the mechanical properties change regularly. The variation of material strength with the size of NB core wire was studied by measuring the stress-strain curves of different wire sizes. The variation characteristics of elastic modulus and nano-indentation value with material size were analyzed by nano-indentation method. The results show that the measured strength of the material is much larger than the theoretical value calculated by the mixed law, and with the decrease of the size of NB core wire, the nano-hardness of Nb-core wire increases exponentially. The interfacial electron scattering related to the electron free path is the main factor affecting the conductivity of the material.
【作者单位】： 西北有色金属研究院;
【基金】：国家自然科学基金(51031002)
【分类号】：TB331

【相似文献】

相关期刊论文 前10条

1 张传立,聂国华;纳米硬度实验中的多位错生成分析[J];力学季刊;2004年04期

2 李直;海尔曼·康拉德;;一种用于微米/纳米硬度测试的具有纳米分辨率的压痕成像系统(英文)[J];纳米技术与精密工程;2008年04期

3 李佳丽,伞金福,王禹,刘家浚;离子注入剂量对工程塑料表面纳米硬度的影响[J];中国表面工程;2005年03期

4 于峰,史立秋,王涛;单晶硅的纳米硬度测试分析[J];金属热处理;2005年08期

5 华文深,吴杏芳,陆华,沈电洪;TiC_x/Ni_3Al复合材料相界面显微结构及界面纳米硬度与弹性模量分布[J];金属学报;2002年10期

6 黎军顽;江五贵;;基于准连续介质法预测薄膜材料纳米硬度和弹性模量[J];金属学报;2007年08期

7 王馨;李荣斌;孙会;;45钢/锡基合金摩擦磨损后表层组织及纳米硬度的表征[J];上海电机学院学报;2014年01期

8 向勇;任杰;白满社;陈静;张晋宽;;Li_2O-Al_2O_3-SiO_2微晶玻璃超光滑表面纳米硬度实验研究[J];纳米技术与精密工程;2014年02期

9 黎明,温诗铸,孟永钢;硅的微观硬度测试研究[J];机械科学与技术;2001年06期

10 张传立;用边界元法分析纳米硬度实验中的位错生成[J];长江大学学报(自科版);2004年Z1期

相关会议论文 前2条

1 杜华;卢明臻;高思田;魏小林;施玉书;崔建军;;压入法纳米硬度测量与亚太国际比对[A];2009中国仪器仪表与测控技术大会论文集[C];2009年

2 刘o，

本文编号：1804432