纤维型吸油材料的制备及其吸油性能的研究

发布时间：2018-04-27 01:36

  本文选题：纤维 + 疏水改性　； 参考：《中国造纸》2017年07期

【摘要】：为探寻一种高效环保的吸油材料,实验选取未漂白针叶木浆纤维及来源广且廉价的二次纤维(旧报纸)、动物纤维(废旧毛衣)作为原料,利用吸藏型吸油机理,采用机械处理和化学改性结合的工艺制备可生物降解的纤维型吸油材料。结果表明,由未漂白针叶木浆纤维、旧报纸、废旧毛衣改性制备的吸油材料对机油的吸油倍率分别为15.8 g/g、12.5 g/g、17.9 g/g,循环使用5次后的吸油倍率还能保持最大值的80%以上;对油品的适用性广,可有效吸附多种油品。
[Abstract]:In order to explore an efficient and environmentally friendly oil-absorbing material, unbleached softwood pulp fiber and secondary fiber (old newspaper and animal fiber (waste sweater) were selected as raw materials, and the oil-absorbing mechanism was used. The biodegradable fibrous oil absorbent materials were prepared by mechanical treatment and chemical modification. The results showed that the oil absorbency of the oil-absorbing materials modified by unbleached softwood pulp fibers, old newspapers and waste sweaters was 15.8 g / g 12.5 g / g 17.9 g / g, respectively. Widely applicable to oil products, can effectively adsorb a variety of oil products.
【作者单位】： 华南理工大学轻工科学与工程学院;
【基金】：国家自然科学基金(31470608) 中央高校基本业务费(201522117)资助项目
【分类号】：TB34;X55

【相似文献】

相关期刊论文 前2条

1 谷庆宝,吴兵,李发生,何绪文,韩梅;可生物降解吸油材料发展现状与研究进展[J];石油化工环境保护;2002年02期

2 王文华;邱金泉;寇希元;赵瑾;王静;张雨山;;吸油材料在海洋溢油处理中的应用研究进展[J];化工新型材料;2013年07期

相关硕士学位论文 前2条

1 谷军军;磁性纳米吸油材料的制备、表征及性能研究[D];南京理工大学;2015年

2 刘晓晖;秸秆改性制备吸油材料[D];大连工业大学;2016年

，

本文编号：1808622