海泡石基金属氧化物复合材料的合成及其光催化性能研究进展

发布时间：2018-05-12 12:41

  本文选题：海泡石 + 海泡石基金属氧化物　； 参考：《材料导报》2017年09期

【摘要】：海泡石比表面积大、孔隙率高,且表面具有一定量的硅羟基基团,这可为其负载金属氧化物如TiO_2、ZnO、Fe_2O_3等提供更多的活性位点,因而它可以作为一种有效载体来制备具有较好吸附性和催化性的复合材料。主要介绍了海泡石基金属氧化物复合材料的不同制备方法,如溶胶-凝胶法、沉淀法、浸渍法;概述了其在提高比表面积、孔容积以及吸附性能等方面具有的优势;并综述了其在液相和气相光催化领域中的应用;介绍了其光催化性能的影响因素及最佳降解效果;最后对其作为生态环境材料的应用进行了前景展望。
[Abstract]:Sepiolite has a large specific surface area, high porosity and a certain amount of silica hydroxyl groups on the surface, which can provide more active sites for its supported metal oxides such as TiO2ZnO / Fe2O3, etc. Therefore, it can be used as an effective carrier to prepare composite materials with good adsorptive and catalytic properties. The preparation methods of Sepiolite based metal oxide composites, such as sol-gel method, precipitation method and impregnation method, are introduced, and their advantages in improving specific surface area, pore volume and adsorption properties are summarized. Its application in the field of liquid and gas phase photocatalysis was reviewed, the influencing factors of its photocatalytic performance and the optimum degradation effect were introduced. Finally, the prospect of its application as ecological environmental material was prospected.
【作者单位】： 中国建筑材料科学研究总院绿色建筑材料国家重点实验室;湘潭源远海泡石新材料股份有限公司;湘潭海泡石科技有限公司;
【基金】：国家科技攻关计划(2016YFC0700902)
【分类号】：O643.36;TB332

【相似文献】

相关期刊论文 前4条

1 陈寿山;刘以寅;;双(甲基环戊二烯基)二芳氧基金属衍生物的合成和光谱[J];化学学报;1982年10期

2 傅云义，，陈铮;镧对Ll_2结构Al_3Ti基金属间化合物显微组织和力学行为的影响[J];稀土;1996年05期

3 杜立华;王立强;王敏敏;覃继宁;吕维洁;张荻;;TiB和TiC对TiAl基金属间化合物显微组织和拉伸性能的影响[J];机械工程材料;2012年12期

4 ;[J];;年期

相关会议论文 前2条

1 高强;赵晓琳;卜显和;;多面体基金属有机骨架的合成与性质研究[A];中国化学会第29届学术年会摘要集——第13分会：晶体工程[C];2014年

2 安东丽;杨鹰;谭庚文;赵娜;沈峗;王娟娟;朱红平;;铜基金属的配体调控:结构与反应行为研究[A];第十六届全国金属有机化学学术讨论会论文集[C];2010年

相关硕士学位论文 前3条

1 潘昌盛;Zr基金属氢化物的氢气纯化及回收性能研究[D];北京有色金属研究总院;2015年

2 杨晓剑;多酸基金属有机配位网络制备及功能性研究[D];东北师范大学;2016年

3 唐笑;铁基金属复合氧化物的合成和性质研究[D];同济大学;2008年

本文编号：1878658